【摘 要】
：
The evolution of inclusions and the formation of acicular ferrite (AF) in Ca–Ti treated steel was systematically investigated after Mg and La addition. The inclusions in the molten steel were Ca–Al–O, Ca–Al–Mg–O, and La–Mg–Ca–Al–O after Ca, Mg, and La add
【机 构】
：
School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beij
论文部分内容阅读
The evolution of inclusions and the formation of acicular ferrite (AF) in Ca–Ti treated steel was systematically investigated after Mg and La addition. The inclusions in the molten steel were Ca–Al–O, Ca–Al–Mg–O, and La–Mg–Ca–Al–O after Ca, Mg, and La addition, re-spectively. The type of oxide inclusion in the final quenched samples was the same as that in the molten steel. However, unlike those in molten steel, the inclusions were Ca–Al–Ti–O + MnS, Ca–Mg–Al–Ti–O + MnS, and La–Ca–Mg–Al–Ti–O + MnS in Mg-free, Mg-containing, and La-containing samples, respectively. The inclusions distributed dispersedly in the La-containing sample. In addition, the average size of the in-clusions in the La-containing sample was the smallest, while the number density of inclusions was the highest. The size of effective inclusions (nucleus of AF formation) was mainly in the range of 1–3 μm. In addition, the content of ferrite side plates (FSP) decreased, while the percent-age of AF increased by 16.2％ due to the increase in the number of effective inclusions in the La-containing sample in this study.
其他文献
The present study initially investigates the kinetics of microwave-assisted grinding and flotation in a porphyry copper deposit. Kin-etic tests were conducted on untreated and microwave-irradiated samples by varying the exposure time from 15 to 150 s. Opt
The novel cast irons of chemical composition (wt％) 0.7C–5W–5Mo–5V–10Cr–2.5Ti were invented with the additions of 1.6wt％ B and 2.7wt％ B. The aim of this work was to study the effect of boron on the structural state of the alloys and phase elemental distrib
Bacterial community dynamics and copper leaching with applied forced aeration were investigated during low-grade copper sulph-ide bioleaching to obtain better bioleaching efficiency. Results illustrated that appropriate aeration improved bacterial concent
The effect of CaCO3, Na2CO3, and CaF2 on the reduction roasting and magnetic separation of high-phosphorus iron ore containing phosphorus in the form of Fe3PO7 and apatite was investigated. The results revealed that Na2CO3 had the most significant effect
The effects of multipass friction stir processing (FSP) and Mg powder addition on the different microstructure parts, including the stir zone (SZ), heat-affected zone (HAZ), and thermomechanically affected zone (TMAZ) of Al 1050 alloy were investigated. M
Iron carbon agglomerates (ICA) are used to realize low-carbon blast furnace ironmaking. In this study, the central composite design based on response surface methodology was used to synergistically optimize the compressive strength, reactivity, and post-r
With the rapid development of 3C industries, the demand for high-thermal-conductivity magnesium alloys with high mechanical performance is increasing quickly. However, the thermal conductivities of most common Mg foundry alloys (such as Mg–9wt％–1wt％Zn) ar
A green method of super-gravity separation, which can enhance the filtration process of bismuth and copper phases, was investig-ated and discussed for the rapid removal of copper impurity from bismuth–copper alloy melts. After separation by the super-grav
Al–Mg alloys are an important class of non-heat treatable alloys in which Mg solute and grain size play essential role in their mech-anical properties and plastic deformation behaviors. In this work, a cyclical continuous expanded extrusion and drawing (C
Multicomponent Al20Cr20Fe25Ni25Mn10 alloys were synthesized using spark plasma sintering at different temperatures (800, 900, and 1000℃) and holding times (4, 8, and 12 min) to develop a high entropy alloy (HEA). The characteristics of spark plasma-synthe