【摘 要】
：
将沙柳木粉经稀酸预处理之后,以1-烯丙基-3-甲基咪唑氯盐(AMIMCl)为液化剂,98%浓硫酸为催化剂,进行单因素试验和正交试验,确定最佳工艺条件为:液化剂∶木粉为13∶1(质量比),
【机 构】
：
内蒙古农业大学理学院,内蒙古农业大学材料科学与艺术设计学院,
论文部分内容阅读
将沙柳木粉经稀酸预处理之后,以1-烯丙基-3-甲基咪唑氯盐(AMIMCl)为液化剂,98%浓硫酸为催化剂,进行单因素试验和正交试验,确定最佳工艺条件为:液化剂∶木粉为13∶1(质量比),反应温度为180℃,反应时间为5h,催化剂用量为1%(wt,质量分数)时,失重率最小为4.57%。同时采用FT-IR和SEM对液化产物的残渣结构和表面形貌进行分析。
After the Salix matsutake powder was pretreated by dilute acid, single factor experiment and orthogonal experiment were carried out using 1-allyl-3-methylimidazolium chloride (AMIMCl) as liquefaction agent and 98% concentrated sulfuric acid as catalyst. The best process conditions are as follows: the weight loss rate of liquefaction agent: wood flour is 13:1 (weight ratio), reaction temperature is 180 ℃, reaction time is 5h and catalyst dosage is 1% (wt, mass fraction). FT-IR and SEM were used to analyze the residue structure and surface morphology of liquefaction products.
其他文献
幼儿期是孩子发展的关键期,那么对于3~4岁的幼儿来说该如何给予正确的引导,以促进其良好个性品质的形成.心理学研究表明:幼儿从3岁开始有了社会性,开始关心周围的小朋友,逐渐
以天然生漆与萜烯基水性聚氨酯共混制备共混乳液.研究了生漆含量对共混乳液稳定性、粒径分布的影响;通过红外光谱(FT IR)、差示扫描量热法(DSC)和扫描电镜(SEM)分析方法表征
采用乙醇-碱法制备冷水可溶(CWS)玉米淀粉。以糊液表观黏度、糊液粘附强力和糊液透明度为指标对不同冷水溶解度的CWS玉米淀粉的糊液性质进行研究,并与工厂常用的氧化淀粉进行
简单介绍了双酚A型环氧树脂(EP)各方面的性能、应用及其传统的增韧改性方法,并叙述了超支化EP的优越性能及主要的合成方法.着重阐述了国内外超支化EP改性双酚A型EP的研究进展
为了获得性能更为优异的纳米TiO_2,采用偶联剂KH-570对纳米TiO_2进行表面改性处理,研究偶联剂用量和温度对改性纳米TiO_2粒子功能单体影响。结果表明,随着硅烷偶联剂用量、温
通过控制溶液浓度,溶剂蒸发温度,溶剂蒸发环境3种结晶条件,利用简单的溶液涂膜方法从热力学的角度深入探究了聚偏氟乙烯(PVDF)各晶相产生的原因以及各晶相的相对含量与结晶形
以往的化学课堂上,实验只起到演示和辅助作用,新课改对学生化学实验技能提出了更高的要求.《铁盐和亚铁盐》是高中必修一金属化合物性质的重要内容,和实验紧密相关,本文围绕
综述了制备具有氨基官能团的磁性纳米材料的研究进展。分别通过使用小分子表面活性剂、合成高分子和天然高分子等制备氨基功能化磁性纳米材料。
The progress in the prepar
采用正交试验方法研究了无烟煤的湿法球磨改性,并将改性煤填充丁苯橡胶(SBR)制备了复合材料.无烟煤球磨改性最佳改性条件为:转速550r/min,时间6h,球配比3∶1,球料比6∶1,改性
含氟丙烯酸酯乳液具有良好的附着力和成膜性,而且由于氟元素极强的电负性和较低极化率赋予聚合物优异性能,主要综述了核壳型含氟丙烯酸酯乳液的聚合原理和最近几年国内对核壳