【摘 要】
：
鎳电解精炼过程中电解液的净化渣—鈷渣含有(％):10～13Ni,1～3Co,1～1.5Fe,0.04Cu,45～50水份,以及少量的鉛鋅等。它是提取鈷的原料。但处理鈷渣的現用流程有許多缺点,必須加以全面改
论文部分内容阅读
鎳电解精炼过程中电解液的净化渣—鈷渣含有(％):10～13Ni,1～3Co,1～1.5Fe,0.04Cu,45～50水份,以及少量的鉛鋅等。它是提取鈷的原料。但处理鈷渣的現用流程有許多缺点,必須加以全面改革。为大幅度提高金属回收率,降低生产成本,改善劳动条件,我們认为,在鈷渣的处理过程中,采用联合萃取法是更为合理的。
Nickel electrolysis process of refining the electrolyte residue - cobalt slag containing (%): 10 ~ 13Ni, 1 ~ 3Co, 1 ~ 1.5Fe, 0.04Cu, 45 ~ 50 water, and a small amount of lead and zinc. It is the extraction of cobalt raw materials. However, there are a number of shortcomings in the current process of treating cobalt slag, which must be fully reformed. In order to significantly increase the metal recovery rate, reduce the production cost and improve the working conditions, we think that it is more reasonable to adopt the joint extraction method in the treatment of cobalt slag.
其他文献
小贝克·休斯顿教授是最好的黑人研究的真正代表,因为他有能力把文本理论与非裔美国人社区起源的历史条件连接起来,即非裔美国人虽遭从非洲赶走却通过强调精神与自传来保持其
前言战后关于铝直接还原法的消息有所报导。在美国对于直接还原法炼铝赞成与不赞成的意见不一,现在据就有用这种方法生产原铝的公司,认为可能节省制造氧化铝的设备和工资,可
一、绪言目前高冰鎳处理方法有:(1)分层熔炼法;(2)水冶法;(3)羧基法;(4)低銅高鎳直接电解法;(5)浮选法。本文針对浮选法加以論述。它比分层熔炼法有很多优点。如改善劳动条
在露天采矿作业中,应用单斗挖掘机进行装载矿岩,已有近百年的历史。随着工业的发展,挖掘机的各个部分也作了多方面的改进和提高;但整体结构与工作特性仍保持其基本形态。由
本电解槽是按苏联发明证书№148244研究而成。为了提高生产率,降低电能消耗和延长电解槽寿命,电解槽中采用垂直插入阳极,水平底和水冷阴极棒。阴极棒穿过侧衬引出。
The el
一、原料性质原料是从粗鎢精矿枱浮脫硫得到的硫化矿。金属矿物有黄铁矿、輝鉍矿、輝鉍鉛矿、輝钼矿、毒砂、黑鎢矿和白鎢;非金属矿物有石英和云母等。原料含McS_2 0.71%、B
我厂采用矿热电炉熔炼铜精矿成冰铜,由于在矿热电炉中,炉料系直接加到深达二米左右的液体溶地上,因此,对入炉炉料要求极为严格,主要是:1.炉料含水应尽可能低,在1%以下;2.炉
目前,铜始极片的装配都是采用人工。这道工序是铜电解车间最繁重的劳动之一。因此,《国立有色金属科学研究所》附属的重有色金属专门设计处(CKBUM)根据巴尔哈什和诺里尔斯克
本文总结了辽阳粒铁(1-13次)试验的经验,指出了回转炉粒铁法的优点和冶炼特点。对原料准备、配料,温度控制,界山位置,炉内气氛和炉渣碱度等从理论和实践的结合上,进行了分析,
在铝电解时,为了净化电解槽废气,通常采用的主要方法之一,是以苏打溶液(碱法)洗涤这种废气,因而生成氟化钠溶液。如向这种氟化钠溶液内添加铝酸盐溶液,同时通入二氧化碳,就