【摘 要】
：
通过对2219铝合金轧制板材的显微组织观察和力学性能测试,研究了3种轧制工艺对其板材显微组织和力学性能的影响。结果表明,轧制过程中的道次压下率对2219铝合金的显微组织和
【机 构】
：
中南大学高性能复杂制造国家重点实验室,中南大学轻合金研究院,中南大学机电工程学院,
论文部分内容阅读
通过对2219铝合金轧制板材的显微组织观察和力学性能测试,研究了3种轧制工艺对其板材显微组织和力学性能的影响。结果表明,轧制过程中的道次压下率对2219铝合金的显微组织和力学性能均有显著影响。在总压下率相同的条件下,经40%、22%、28%的热轧,然后进行20%、25%、33%、35%、23%冷轧的板材综合力学性能最好,其抗拉强度、屈服强度、伸长率和维氏硬度分别为406.4 MPa、312.2 MPa、13.4%、169.6 HV。
The effects of three rolling processes on the microstructure and mechanical properties of 2219 aluminum alloy rolled sheet were studied by observing the microstructure and testing the mechanical properties. The results show that the reduction of pass during rolling has a significant effect on the microstructure and mechanical properties of 2219 aluminum alloy. Under the condition of the same total reduction rate, the mechanical properties of the sheet rolled by 40%, 22%, 28% hot rolling followed by 20%, 25%, 33%, 35% and 23% Tensile strength, yield strength, elongation and Vickers hardness were 406.4 MPa, 312.2 MPa, 13.4%, 169.6 HV, respectively.
其他文献
初中物理的目的是训练学生形成科学的思维模式，并逐步参照实际现象掌握理性知识。基于实验的物理教学大大提高了学生自主探索的积极性和自主学习能力。教师可以充分发挥教师在
随着气田开发的深入,苏里格气田致密气开发具有良好前景。但随着日益增长的环保和征地要求以及低成本开发的,越来越多的气井采用水平井大井丛进行开发,过去常规开发模式不能很好的适用于水平井大井丛开发。为研究适用于水平井大井丛开发,对相关地面工艺进行了研究。集气站站内前期运行时不增压,集气站内集中注醇,采气管线进站压力3.6Mpa,出站压力3.5Mpa;后期运行时增压,站内不注醇。采气管线采用双压力系统,干管由一根改为两根小管线,并根据开发时期进行灵活调整,选择最经济的压力系统进行开发。同时根据当地煤炭区、规划区情
众多的 AV 发烧友都意识到,目前最为理想的家庭影院,是由高清晰的 DVD 影碟机为影音源配置而成的杜比数码或 DTS 影院系统。拥有这样一套自己的家庭影院,足不出户便可享受视
77％丰护安可湿性粉剂是德国优乐利农化有限公司产品,属铜制剂类杀菌剂。1994年在广西南宁市北湖园艺场对7年生的甜橙进行的防治溃疡病试验设77％丰护安600倍、480倍、400倍液,7
“十一五”期间,全省住房和城乡建设系统认真贯彻落实中央和省委、省政府的各项决策部署,统筹城乡发展、着力改善民生,完善市场监管、建设宜居环境,如期实现了“十一五”各项
随着我国新课程改革的不断深入和发展，小学阶段的课堂教学越来越重视学生的体验和主体地位。本文以小学语文阅读教学为例，阐述了情境体验的概念和内涵，分析了情境体验在小学语文
苏里格气田是受三角洲平原分流河道砂体控制的大面积分布的低压、低渗透、低丰度岩性气田。岩性致密,储层物性差,非均质性强,横向连通性差,使得准确预测气井产能较困难。目前用于确定低渗透气井产能方程的方法存在诸多局限性。以气井产能方程为基础,研究影响产能因素,根据各参数敏感程度,判断产能主要影响因素为地层系数。为减小束缚水和残余气的影响,提出了基于归一化相对渗透率模型的有效地层系数,建立基于有效地层系数的气井产能预测方程。该方法在苏76区块进行验证,预测的无阻流量与测试无阻流量符合率在82%以上,符合气井的实际生