Mg matrix composites with SiC particles ranging from 5vol%-25vol% were prepared using stirring casting method. Die casting, squeezing casting, and extrusion were applied for inhibiting or eliminating the defects such as gas porosity and shrinkage void. Through die casting and squeezing casting, most of the defects in Mg matrix composites could be eliminated, but the mechanical properties were improved limitedly. On the other hand, after hot extrusion, not only most of the defects of as-cast composites ingots were eliminated, but also the mechanical properties were improved markedly. With the addition of SiC, the tensile strength, yield strength and elastic modulus of as extrusion SiCp/AZ61 composites increased remarkably, and the elongation decreased obviously.
Mg matrix composites with SiC particles ranging from 5vol% -25vol% were prepared using stirring casting method. Die casting, squeezing casting, and extrusion were applied for inhibiting or eliminating the defects such as gas porosity and shrinkage void. Through die casting and squeezing casting , most of the defects in Mg matrix composites could been eliminated, but the mechanical properties were improved limited. On the other hand, after hot extrusion, not only most of the defects as as cast composites ingots were eliminated, but also the mechanical properties With the addition of SiC, the tensile strength, yield strength and elastic modulus of as extruded SiCp / AZ61 composites were remarkably, and the elongation decreased obviously.