The effects of erosive parameters,such as impact angles and environment temperature,on erosion properties of FeBSiCrMnNb nanoscale coatings were investigated.A series of coatings were prepared by wire arc spraying process.The microstructure of the coating consists of amorphous andα(Fe,Cr)nanocrystalline phase.The nanocrystals with average size of 39 nm are homogenously dispersed in amorphous matrix.The erosion results reveal that the coating exhibits better erosion resistance at lower impact angle.The erosion rates of the coating decrease as function of environment temperature.The relatively erosion resistance of the nanoscale coating is 3.7 times higher than that of AISI1045 steel substrate at 650°C.The main failure mechanism of the coating is brittle fracture.
The effects of erosive parameters, such as impact angles and environment temperature, on erosion properties of FeBSiCrMnNb nanoscale coatings were investigated. A series of coatings were prepared by wire arc spraying process. The microstructure of the coating consists of amorphous and α (Fe, Cr) The erosion results reveal that the coating exhibits better erosion resistance at lower impact angle. The erosion rates of the coating decrease as function of environment temperature. The more erosion resistance of the nanoscale coating is 3.7 times higher than that of AISI 1045 steel substrate at 650 ° C. The main failure mechanism of the coating is brittle fracture.