The cathode material La1-xSrxCuO3-δ(x=0.15, 0.2, 0.3, 0.4) was synthesized by a sol-gel method. X-ray diffraction reveals that a single phase of perovskite is formed. The investigation of the electrical properties suggests that La0.7Sr0.3CuO3-δ has the highest electrical conductivity. La0.7Sr0.3CuO3-δ powder was mixed with different amount SDC (Sm0.15Ce0.85O1.925) powder (5wt.%-30wt.%) as composite cathodes. Electrochemical properties of the composite cathodes were researched further. Investigation suggests that the addition of appropriate amount SDC to La0.7Sr0.3CuO3-δ can improve the electrochemical properties and obtain better cathodic performance. Using La0.7Sr0.3CuO3-δ-SDC composite materials as a cathode based on SDC electrolyte, higher current density and power density at intermediate temperatures can be obtained.
The cathode material La1-xSrxCuO3- δ (x = 0.15, 0.2, 0.3, 0.4) was synthesized by a sol-gel method. X-ray diffraction reveals that a single phase of perovskite is formed. The investigation of the electrical properties suggests that La0.7Sr0.3CuO3-δ has the highest electrical conductivity. La0.7Sr0.3CuO3-δ powder was mixed with different amount of SDC (Sm0.15Ce0.85O1.925) powder (5wt.% - 30wt.%) As composite cathodes. Electrochemical properties of the composite cathodes were researched further. Investigation suggests that the addition of the appropriate amount SDC to La0.7Sr0.3CuO3- δ can improve the electrochemical properties and obtain better cathodic performance. Using La0.7Sr0.3CuO3-δ-SDC composite materials as a cathode based on SDC electrolyte, higher current density and power density at intermediate temperature can be obtained.