Five non stoichiometric alloys, i.e., LaNi 5.15 , La(NiSn) 5.14 , La(NiSnCo) 5.12 , La(NiSnMn) 5.12 , and La(NiSnCoMnAl) 5.10 were studied. It is shown that the second minor phase does not exist in the major phase through the X ray diffraction analysis. By the measurements of the crystal lattice constant, the volume of crystal lattice decreases with the increasing of the amount of atom B in AB 5. It is more obvious when the element nickel in B is partially subsituted by other elements. For non stoichiometric alloys, the lattice volume greatly increases when Ni is partially substituted by Sn. The lattice constant is also effected by the addition of Mn, Co, and Al. By means of electrochemical measurements, the plateau pressure of hydrogen absorption/desorption is measured with the results that Sn, Co, Mn and Al decrease the plateau pressure.
LaNi 5.15, La (NiSn) 5.14, La (NiSnCo) 5.12, La (NiSnMn) 5.12, and La (NiSnCoMnAl) 5.10 were studied. It is shown that the second minor phase does not exist in the major phase through the X ray diffraction analysis. By the measurements of the crystal lattice constant, the volume of crystal lattice decreases with the increasing of the amount of atom B in AB 5. It is more obvious when the element nickel in B is partially subsituted For nonstoichiometric alloys, the lattice volume greatly increases when Ni is partially substituted by Sn. The lattice constant is also effected by the addition of Mn, Co, and Al. By means of electrochemical measurements, the plateau pressure of hydrogen absorption / desorption is measured with the results that Sn, Co, Mn and Al decrease the plateau pressure.