论文部分内容阅读
It is expected that the welding hardfacing of continuous casting rolls has better welding performance and higher wear resistance. A new type of submerged-arc hardfacing flux-cored wire has been developed through nitrogen replacing part of carbon and addition of the nitrogen-fixing elements of niobium and titanium. And microstructure, degree of hardness and high-temperature wear resistance of its deposited metal samples were also investigated. It is found that the microstructure is martensite, residual austenite and carbonitride precipitates. As a result, the hardfacing metal with homogeneous distribution of very fine carbonitride particles had high hardness and excellent wear-resisting property during high-temperature wear, which could significantly extend the service life of continuous casting rolls.
It is expected that the welding hardfacing of continuous casting rolls has better welding performance and higher wear resistance. A new type of submerged-arc hardfacing flux-cored wire has been developed through nitrogen replacing part of carbon and addition of the nitrogen-fixing elements of And microstructure, degree of hardness and high-temperature wear resistance of its deposited metal samples were also investigated. It is found that the microstructure is martensite, residual austenite and carbonitride precipitates. As a result, the hardfacing metal with homogeneous distribution of very fine carbonitride particles had high hardness and excellent wear-resisting property during high-temperature wear, which could significantly extend the service life of continuous casting rolls.