,Enhanced selective catalytic reduction of NO with NH3 via porous micro-spherical aggregates of Mn-C

• 作 者: Junqi Tian Ke Zhang Wei Wang Fu Wang Jianming Dan Shengchao Yang Jinli Zhang Bin Dai Feng Yu
• 机 构: Key Laboratory for Green Processing of Chemical Engineering of Xinjiang Bingtuan, School of Chemistr
• 出 处: 绿色能源与环境（英文）
• 发表日期: 2019年3期
• 关键词: Mn-Ce-Fe-Ti mixed oxide Porous microspheres Spray drying Selective catalytic red

We rationally designed a high performance denitration (De-NOx) catalyst based on a micrometer-sized spherical Mn-Ce-Fe-Ti (CP-SD) catalyst for selective catalytic reduction (SCR).This was prepared by a co-precipitation and spray drying (CP-SD) method.The catalyst was systematically characterized,and its morphological structure and surface properties were identified.Compare with conventional Mn-Ce-Fe-Ti (CP) catalysts,the Mn-Ce-Fe-Ti (CP-SD) catalyst had superior surface-adsorbed oxygen leading to enhanced "fast NH3-SCR" reaction.The asobtained Mn-Ce-Fe-Ti (CP-SD) catalyst offered excellent NO conversion and N2 selectivity of 100.0％ and 84.8％ at 250 ℃,respectively,with a gas hourly space velocity (GHSV) of 40,000 h-1.The porous micro-spherical structure provides a larger surface area and more active sites to adsorb and activate the reaction gases.In addition,the uniform distribution and strong interaction of manganese,iron,cerium,and titanium oxide species improved H2O and SO2 resistance.The results showed that the Mn-Ce-Fe-Ti (CP-SD) catalyst could be used prospectively as a denitration (De-NOx) catalyst.