Copper oxides were prepared by direct heating and decomposing copper(Ⅱ) salts, such as Cu 2(OH) 2CO 3, Cu(NO 3) 2·3H 2O, Cu 2C 6H 4O 7·2 5H 2O, CuC 2O 4·2H 2O and CuAc 2·H 2O. The phase, surface area and catalytic activity of the oxides for H 2O 2 decomposition were investigated by means of XRD and BET measurements. It has been demonstrated that the characteristics of copper oxides obtained from different precursors are much different from each other. Monocomponent nano CuO, which has higher catalytic activity for H 2O 2 decomposition, can be prepared by direct heating and decomposing Cu 2(OH) 2CO 3. On the other hand, CuO in the decomposition products of the organic acid copper can be partially reduced to Cu 2O and Cu in the reducing atmosphere, and the Cu 2O component in the products has higher catalytic activity for H 2O 2 decomposition.
Copper oxides were prepared by direct heating and decomposing copper (II) salts such as Cu 2 (OH) 2CO 3, Cu (NO 3) 2 · 3H 2O, Cu 2C 6H 4O 7 · 2 5H 2O, CuC 2O 4 · 2H 2O and CuAc 2 · H 2O. The phase, surface area and catalytic activity of the oxides for H 2O 2 decomposition were investigated by means of XRD and BET measurements. It has been demonstrated that the characteristics of copper is obtained from different precursors are much different from each other. Monocomponent nano CuO, which has higher catalytic activity for H 2 O 2 decomposition, can be prepared by direct heating and decomposing Cu 2 (OH) 2CO 3. On the other hand, CuO in the decomposition products of the organic acid copper can be partially reduced to Cu 2O and Cu in the reducing atmosphere, and the Cu 2O component in the products has higher catalytic activity for H 2O 2 decomposition.