A kind of nanokaolin powder with a thickness of 20-50nm and an average diameter of 300nm is produced through combined procedure of purification, delamination, surface modification and pulverization. The application experiments in butadiene rubber (BR), ethylene-propylene diene methylene (EPDM), and natural rubber (NR) indicates that this nano-kaolin powder material is much better than precipitated silica in reinforcement, while in styrene-butadiene rubber (SBR) it is close to precipitated silica. Nanokaolin is of superiority in elasticity, elongation at break, anti-flexure property.
The application experiments in butadiene rubber (BR), ethylene-propylene diene methylene (EPDM ), and natural rubber (NR) indicates that this nano-kaolin powder material is much better than precipitated silica in reinforcement, while in styrene-butadiene rubber (SBR) it is close to precipitated silica. break, anti-flexure property.