Current—voltage (I—V) and capacitance-voltage (C—V) characteristics of Au/p-CZT contacts with different surface treatments on cadmium zinc telluride (CZT) wa
【机 构】
：
College of Materials Science and Engineering
论文部分内容阅读
Current—voltage (I—V) and capacitance-voltage (C—V) characteristics of Au/p-CZT contacts with different surface treatments on cadmium zinc telluride (CZT) wafers surface were measured with Agilent 4339B high resistance meter and Agilent 4294A precision impedance analyzer,respectively. The Schottky barrier height was 0.85±0.05,0.96±0.05 eV for non-passivated and passivated CZT crystals by I—V measurement. By C—V measurement,the Schottky barrier height was 1.39±0.05,1.51±0.05 eV for non-passivated and passivated CZT crystals. The results show that the passivation treatment can increase the barrier height of the Au/p-CZT contact and decrease the leakage current. The main reason is that the higher barrier height of Au/p-CZT contacts can decrease the possibility for electrons to pass through the native TeO2 film. Most of the applied voltage appears on the depleted layer and there is only a negligible voltage drops across the nearly undepleted region. Furthermore,the electric field in the depleted layer is not uniform and can be calculated by the depletion approximation. The maximum electric field of CZT crystals is Em1=133 V/cm at x=0 for non-passivated CZT crystal and Em2=55 V/cm for passivated CZT crystal,respectively.
其他文献
One way of improving the magnetic properties of RECo5 (RE=rare earth) compounds, especially the magnetic anisotropy energy (MAE), is to dope them with some addi
The optical properties of blue emitting BaAl2S4:Eu thin-films were studied. The emission peak is around 470 nm, whose FWHM (full width at half maximum) is 35 nm
Transparent polycrystalline yttria is a promising optical ceramics with excellent physical and chemical properties. A commercial yttria powder with a mean parti
The formation ability and thermal stability of phosphate laser protection glass doped with high Sm2O3 content were discussed. The characteristic temperatures (T
316L stainless steel samples,as a widespread used material,were irradiated with HIPIB at the beam parameters of ion energy 300 keV,current density 100,200 and 3
The existence of yttrium in Ti-23Al-25Nb alloy and its influence on the microstructure after heat treatment of Ti-23Al-25Nb alloy were investigated using therma
Dipolar relaxation and dielectric/piezoelectric resonance in a (001)-cut Pb(Zn1/3Nb2/3)0.9Ti0.1O3 (PZNT10%) single crystal before and after electric (E)-field p
Three different coatings, Cr, SiO2/Cr and HfO2/SiO2 were deposited by electron beam physical vapor deposition (EB-PVD). Relevant composition and mechanical prop
A novel Al-based composite material (Al63Cu25Fe12)p/A356 was prepared by spray co-deposition. It is revealed that the reinforcement of Al63Cu25Fe12 quasicrystal
The corrosion behavior of a CuCrNiAl alloy in HCl solutions was studied by means of metallograph, XRD, SEM/EDX and TEM methods. The results show that in low con