Effects of V and Zr Additions on Microstructures and Mechanical Properties of Nb-Ti-Al-Base Alloys

• 出 处: 稀有金属材料与工程
• 发表日期: 2009年S3期
• 关键词: ductility tensile have melting equiaxed precipitated titanium refined carbide st

Microstructures and mechanical properties of Nb-32Ti-7Al alloys containing different V and Zr contents were investigated. The microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The alloy with V and Zr presents single phase Nb solid solution (Nbss). Tensile testing was carried out at room temperature and 1373 K. The results show that these alloys have good ductility at room temperature. The strengths at room and high temperature increase with the addition of V and Zr, but the room temperature ductility decrease.

Microstructures and mechanical properties of Nb-32Ti-7Al alloys containing different V and Zr contents were investigated. The microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The alloy with V and Zr presents single phase Nb solid solution (Nbss) Tensile testing was carried out at room temperature and 1373 K. The results show that these alloys have good ductility at room temperature. The strengths at room and high temperature increase with the addition of V and Zr, but the room temperature ductility decrease.