采用正交实验设计 ,以测定硫酸铝钾 [KAl(SO4 ) 2 ]的含量为考察指标 ,筛选以烘制法炮制枯矾的最佳条件。结果 :温度 2 4 0℃ ,时间 1 5h ,样品粒度 5mm是烘制法炮制枯矾的最佳条件。优选出的制法为今后枯矾炮制的规范化提供了参考依据
Orthogonal experimental design was used to determine the content of potassium aluminum sulfate [KAl(SO4)2] as the inspection index, and the best conditions for drying the dried haze with baking method were selected. RESULTS: The temperature was 240°C, the time was 15h, and the sample particle size of 5mm was the best condition for the drying process. The preferred method provides a reference for the standardization of dry processing in the future