【摘 要】
：
高速钢分级淬火时,为了防止开裂和减少变形,采用580～620℃分级冷却。这就要求分级盐浴熔点至少应低于560℃,才能有效地保证生产顺利进行,稳定产品质量。在实际生产中,一般用5
论文部分内容阅读
高速钢分级淬火时,为了防止开裂和减少变形,采用580～620℃分级冷却。这就要求分级盐浴熔点至少应低于560℃,才能有效地保证生产顺利进行,稳定产品质量。在实际生产中,一般用50％BaCl_2+30％KCl+20％NaCl(以下简称235盐)作为分级盐浴,并且也作为添加补充用。但使用一段时间后,盐浴熔点升高,这是由于淬火时从高温炉中带出BaCl_2到分级盐浴中去,使其中
High speed steel grade quenching, in order to prevent cracking and reduce deformation, using 580 ~ 620 ℃ classification cooling. This requires grading salt bath melting point should be at least below 560 ℃, in order to effectively ensure the smooth production and stable product quality. In actual production, 50% BaCl 2 + 30% KCl + 20% NaCl (hereinafter referred to as 235 salt) is generally used as a graded salt bath, and is also used as an addition supplement. However, after a period of time, salt bath melting point increased, which is due to the quenching furnace out of the high-temperature furnace BaCL_2 to grading salt bath so that
其他文献
激情哪里去了？他深情地注视着你，手从你的颈后滑向背后。你们的情话和亲吻没完没了，火一样的爱。人过30岁，已经大多没有这样长时间的性抚慰了，他们已经知道如何熟练地进入佳境了。
非对称信息是指某些参与人拥有而某些参与人不拥有，并由上市公司中的会计人员通过一定的途径传播给相应使用者的信息。上市公司的信息提供者基于利益、权力、责任、公信度等诸多方面的考虑，自觉或不自觉地隐藏某些信息，从而使包括股东在内的其他信息使用者就不能掌握自己的投资抉择某个上市公司在股票市场的全部信息，导致不对称现象。 随着我国起始于2005年股权分置改革的基本完成，我国证券市场最大的“一股独大”的制度
本文用 X 射线衍射法,对锻铝激光表面处理前后的衍射图样进行了比较分析。并对图样的变化及其所引起的性能差异作了论述。同时,对激光表面处理后的锻铝进行了相分析,测得了 A
人活在世上 ,总要不时地与自己打交道。不是人人都能成为“心如明镜台”的慧明禅师或是梦中迷蝶的庄周的 ,因此人对自己总抱有一定的看法。有人生活在自卑的阴影中 ,有人自负
An intracavity frequency-doubled vertical external cavity surface emitting laser(VECSEL)with green light is demonstrated.The fundamental frequency laser cavity
概略:略述了在铁合金中测定主要元素的方法。铁合金是铁和一种或多种其他元素所组成的合金,它主要用于将合金金属按某一比例加到熔融状态钢水的钢包中,以给出在最终产品中确
高炉铁液经变质处理后,原生铁中粗大片状石墨成为球状或蠕团状,从而使其抗拉强度由～10kg/mm~2提高至35～63kg/mm~2,用它制取铸件是一种节能的生产方式。但变质高炉铁液直接用于
在机器制造业中,孔加工的零件是很普遍的,但在加工过程中,由于各种因素的影响,往往满足不了精度要求,因此,必须经常对刀具进行调整,但微调机构的形式很多,现选择介绍几种不
每年的大中专(职校)毕业生,只要一迈出校门,就面临着求职、应聘的问题。要想在激烈的竞争中找到满意的单位和获得较高收入,除了有相应的文凭外,应聘时“细节”也不能忽略。
北京液压机械厂参照西德派纳公司的液压抓具的工艺和制造技术,研制了0.8m~3和1.0m~3两种规格的液压抓具。0.8m~3抓具现已在首钢使用。1.Om“抓具在上钢一厂试验后,现准备去