【摘 要】
：
The influences of heat treatment and test condition on the microstructure and stress rupture properties of a Ni-Mo-Cr-Fe base corrosion-resistant superalloy have been investigated in this paper.Optical microscope and scanning electron microscope were empl
【机 构】
：
Jiangsu University of Technology, Changzhou 213001, China;Harbin Engineering University, Harbin 1500
论文部分内容阅读
The influences of heat treatment and test condition on the microstructure and stress rupture properties of a Ni-Mo-Cr-Fe base corrosion-resistant superalloy have been investigated in this paper.Optical microscope and scanning electron microscope were employed for the microstructure observation,and X-ray diffraction,electron probe micro-analyzer,and transmission electron microscope were used for phase determination.It was found that the grain size increased and the volume fractions of initial M6C carbides decreased along with the increase in solution treatment temperature.When tested at 650 ℃/320 MPa,the stress rupture lives decreased with the increase in solution treatment temperature,but the stress rupture lives increased slightly at first and then decreased for the samples solution heat treated at 1220 ℃ when tested at 700 ℃/240 MPa.The elongations showed the descendent trends under these two conditions.The stress rupture life and elongation for the aged samples all showed a noticeable improvement at 650 ℃/320 MPa,but there was no noticeable improvement at 700 ℃/240 MPa.The reasons can be attributed to the grain size,test conditions,and the initial and secondary carbides.
其他文献
To understand the atomistic mechanisms of tension failure of Ni-based superalloy,in this study,the classical molecular dynamics (MD) simulations were used to study the uniaxial tension processes of both the Ni/Ni3Al interface systems and the pure Ni and N
In the present work,the electrochemical behavior and properties of the passive film of a new Sn-alloyed 316LX austenitic stainless steel were investigated.With the increase in Sn content in 316LX austenitic stainless steel from 0 to 0.21％,the critical pit
Mg-2Al-1.2Ca-0.2Mn (at％)-based alloys with Ce-rich mischmetal (MM) substitution of 0-0.6 at％ for Ca were hot extruded at 400 ℃.The effect of MM substitution on the microstructure and mechanical properties of the extruded alloys was investigated.The as-cas
The high-current pulsed electron beam (HCPEB) treatment with current density 6 J/cm2 was applied on AZ91 Mg alloy to improve its corrosion resistance.Results showed that the net-like Mg17Al12 disappeared on the surface of AZ91 Mg alloy after irradiation b
The effect of lead on the initial corrosion behavior of 316LN stainless steel has been investigated by U-bend immersion experiments in 4 wt％ NaOH solutions at 300 ℃.Follow-up studies after soaking were carried out by scanning electron microscope,energy di
In this work,the effect of prior cold deformation on the stability of retained austenite in GCr15 bearing steel was investigated after quenching and tempering treatment.The thermal stability was evaluated by calculating thermal activation energy for decom
Mg AZ31/Al 7050 laminate was fabricated by co-extrusion directly from the as-cast Mg AZ31 and Al 7050 billets.The influence of annealing temperature and annealing time on microstructure and mechanical behavior of the extruded Mg/Al laminate was systematic
The AZ31 Mg alloys were processed by 6％ pre-compression and frustum shearing extrusion at various temperatures,and the microstructure,texture and mechanical properties of the resulting alloys are systematically investigated.The results show that the grain
The rupture behavior of the modified 10Cr-lMo steel multi-layer welded joint is determined by the fine-grain zones of the weld metal adjacent to the fusion line during the long-term creep test at 620 ℃.The microstructures of multi-layer weld metal before
The tensile creep behavior of extruded Mg-6Gd alloy,having the tensile yield strength of ～ 110 MPa at 175 ℃,has been investigated under 175 ℃ and 150 MPa.In this study,the extruded Mg-6Gd sample exhibits the total tensile strain of ～ 10.5％ after the creep