Surface modification of up-conversion luminescence materials (Na[Y_(0.57)Yb_(0.39)Er_(0.04)]F_4 modified by amino groups) by grafting and modify- ing with aldehyde groups was studied by means of Fourier transform infrared spectroscopy (FTIR),scanning electron microscopy (SEM), thermogravimetdc analysis (TGA),and emission spectrum (EM).The surface modification effect was compared using two different finish- ing agents,p-phthalaldehyde and glutaraldehyde.It was found that the surface of up-conversion luminescence materials could be modified by aldehyde groups of the two finishing agents,the systematic dispersibility and the thermostability of the up-conversion luminescence material modified by p-phthalaldehyde were better than those of the material modified by glutaraldehyde,and the luminous intensity of the material modified by p-phthalaldehyde was increased.The AI (the ratio of the suspended segmental quality in the specimen to the total mass of the specimen) of the material modified by p-phthalaldehyde was higher than that of the material modified by glutaraldehyde.It is obviously seen that the embellishment effect of p-phthalaldehyde as a finishing agent was better than that of glutaraldehyde.In addition,the reasons why p-phthalaldehyde is a good finishing agent are also explained.
Surface modification of up-conversion luminescence materials (Na [Y_ (0.57) Yb_ (0.39) Er_ (0.04)] F_4 modified by amino groups) by grafting and modify- ing aldehyde groups was studied by means of Fourier transform infrared spectroscopy scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and emission spectrum (EM) .The surface modification effect was compared using two different finish- ing agents, p-phthalaldehyde and glutaraldehyde. It was found that the surface of up -conversion luminescence materials could be modified by aldehyde groups of the two finishing agents, the systematic dispersibility and the thermostability of the up-conversion luminescence material modified by p-phthalaldehyde were better than those of the material modified by glutaraldehyde, and the luminous intensity of the material modified by p-phthalaldehyde was increased. The AI (the ratio of the suspended segmental quality in the specimen to the total mass of the specimen) of the material modified b y p-phthalaldehyde was higher than that of the material modified by glutaraldehyde. It is obvious that that the embellishment effect of p-phthalaldehyde as a finishing agent was better than that of glutaraldehyde. In addition, the reasons why p-phthalaldehyde is a good finishing agent are also explained.