  5. Green corrosion inhibitors intercalated Mg∶Al layered double hydroxide coatings to protect Mg alloy

Green corrosion inhibitors intercalated Mg∶Al layered double hydroxide coatings to protect Mg alloy

来源 :稀有金属:英文版 | 被引量 : 0次 | 上传用户：hulin99
【摘 要】
：
Mg alloy was protected with Mg:Al layered double hydroxide(LDH)coating intercalated with three green corrosion inhibitors(sodium benzoate,3-aminopropyltriethoxysilane and 8-hydroxyquinoline).The in-situ hydrothermal approach was adopted to intercalate cor
【作 者】
：
Muhammad Junaid Anjum Jing-Mao Zhao Vahdat Zahedi Asl Muhammad Uzair Malik Ghulam Yasin Waheed Qamar Khan 
【机 构】
：
CollegeofMaterialsScienceandEngineering,BeijingKeyLaboratoryofElectrochemicalProcessandTechnologyfor
【出 处】
：
稀有金属:英文版
【发表日期】
：
2021年8期
【关键词】
：
MAGNESIUM Layered double hydroxide coating Organic inhibitors INTERCALATION Corr 
【基金项目】
：
financially supported by the National Natural Science Foundation of China(No.51471021)。
下载到本地 , 更方便阅读
下载此文 赞助VIP
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Mg alloy was protected with Mg:Al layered double hydroxide(LDH)coating intercalated with three green corrosion inhibitors(sodium benzoate,3-aminopropyltriethoxysilane and 8-hydroxyquinoline).The in-situ hydrothermal approach was adopted to intercalate cor
其他文献
中高频椭圆铰链双光纤光栅加速度传感器
针对现有光学传感器难以满足大型结构中高频振动监测的需求,提出一种基于椭圆铰链的中高频双光纤布拉格光栅加速度传感器。基于传感器理论模型分析传感器的灵敏度和谐振频率,采用MATLAB和ANSYS软件对传感器的结构参数进行优化及仿真,研制双光纤布拉格光栅传感器,并进行传感器灵敏度标定实验。结果表明:传感器的谐振频率约为780 Hz,灵敏度为132.53 pm/g,横向抗干扰度小于3.3%,可用于80~500 Hz之间振动信号的实时监测。
期刊
光纤传感器光纤布拉格光栅(FBG)椭圆铰链中高频
Hot pressing sintering process and sintering mechanism of W-La2O3-Y2O3-ZrO2
The W-La2O3-Y2O3-ZrO2materials were prepared by vacuum hot pressing sintering process.The microstructure was characterized by scanning electron microscopy(SEM).The effects of sintering temperature,sin
期刊
W-La_(2)O_(3)-Y_(2)O_(3)-ZrO_(2)HotpressingsinteringRelativedensityTungste
Deposition and characterization for high-quality Ti-Ni-Cu thin films with higher Cu content
In order to attain high-quality Ti-Ni-Cu film,the surface morphologies,chemical compositions and mechanical properties of Ti-Ni-Cu thin films prepared by direct current(DC)magnetron sputtering at various processes were characterized by scanning electron m
期刊
Ti-Ni-CuthinfilmDCmagnetronsputteringSputteringparametersChemicalcompos
Enhanced strength and electrical conductivity of Al-0.3Ce alloy simultaneously with Ti(C,N)nanoparti
Ti(C,N)nanoparticles were added to an Al-0.3 Ce alloy by ultrasonic treatment.Further annealing at 570℃for4 h afforded the ultimate tensile strength of 79 MPa and electrical conductivity of 64.0%IACS for the Al-0.3 Ce alloy with1.5 vol%Ti(C,N)addition.Bot
期刊
ConductivealuminumalloyTi(CN)nanoparticlesCeMicro-nanohierarchicalspheri
Zr55Al10Ni5Cu30 amorphous alloy film prepared by magnetron sputtering method
In this work,amorphous Zr55Al10Ni5Cu30 alloy thin film was prepared on D36 steel substrate by magnetron sputtering method.The film was characterized by scanning
期刊
Magnetron sputteringAmorphous alloyThin filmCorrosion resistanceZr55Al10Ni5C
High-temperature corrosion of Sn-Bi-Zn-Ga alloys as heat transfer fluid
The new heat transfer alloy is highly reactive at high temperatures,and the corrosion of the container mate-rial determines the service life of the heat transfe
期刊
Sn-Bi-Zn-GaHeat transfer fluidsThermophysical propertiesHigh-temperature corr
Microstructure and corrosion properties of Mg-0.5Zn-0.2Ca-0.2Ce alloy with different processing cond
The microstructure and corrosion resistance of Mg-0.5 Zn-0.2 Ca-0.2 Ce alloy with different processing conditions were investigated.The composition was detected by X-ray fluorescence(XRF),and the microstructure was analyzed by optical microscopy(OM)and sc
期刊
Mg-0.5Zn-0.2Ca-0.2CealloyProcessingconditionsTEXTURECorrosionbehavior
Zn-Fe and Y-modified Zn-Fe coatings on 42CrMo steel via pack cementation
Zn-Fe and Y-modified Zn-Fe coatings were prepared on 42 CrMo steel through pack cementation processes at 370,390 and 410℃for 4 h.Y modification was achieved through the co-deposition of Zn and Y2 O3.The effects of Y modification on microstructure,formatio
期刊
PackcementationCOATINGMODIFICATIONActivationenergyCORROSION
Chip morphology and cutting temperature of ADC12 aluminum alloy during high-speed milling
The ADC12 aluminum alloy is prone to severe tool wear and high cutting heat during high-speed milling because of its high hardness.This study analyzes the highspeed milling process from the perspective of different chip morphologies.The influence of cutti
期刊
ADC12aluminumalloyHigh-speedmillingChipmorphologyCuttingtemperatureFini
Microstructure and properties of Inconel 625 + WC composite coatings prepared by laser cladding
Inconel 625+WC composite coatings were prepared on the surface of 2Cr13 steel by laser cladding.The microstructure,microhardness and corrosion resistance of the composite coatings with different WC contents were investigated in detail.The results show tha
期刊
LasercladdingWCcontentInconel625ElectrochemicalcorrosionMICROHARDNESS