Multilayer hard coatings of TiC/Ti(C,N)/TiN on 35CrMo steel substrates were deposited by a chemical vapor deposition system(CVD).X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy disper-sive X-ray spectrometer(EDX)were used to analyze phase composition,morphology,and chemical composition of the coatings.The mechanical,corrosion,and wear prop-erties of the produced coatings were primarily examined.The results indicate that multilayer coatings are consisted of TiC,Ti(C0.2N0.8),and TiN.The coatings surface is dense,and the thickness is about 11 μm.The adhesion between coatings and steel substrate was characterized by critical load(Lc)and is found to be about 70 N.The mi-crohardness of the multilayer coatings is HV 2400,which is about 5 times as that of the 35CrMo steel substrate.The corrosion current of the coated sample is 4.368 x 10-5 A·cm-2,which decreases by one order of magnitude compared with the uncoated one(1.324 × 10-4 A·cm-2).Friction and wear tests show that the TiC/Ti(C,N)/TiN coatings with high hardness adhere well to the 35CrMo substrate and display good wear resistance and low friction coefficient under non-lubricated friction test at room temperature.