The mechanism of additive ZC 1 for catalyzing combustion of coke breeze in sintering of iron ore fines was studied by using X ray Diffraction, TGA and GC(Gas Chromatographer), by which energy saving was achieved on sinter pot test. The results show that the distance between cleavage planes is enlarged and the π electrons are re distributed because of the insertion of cations/molecules of ZC 1 into the cleavage planes of carbon , resulting in the weakening of C-C bond, improving the adsorption of oxygen and lowering the activation energy of gasification of carbon from 25.8 kJ/mol to 18.9 kJ/mol , and the burning rate being increased and combustion residual reduced, all of which can lead to lower solid fuel consumption . Compared with the sintering test without addition of additives , the solid fuel consumption is reduced by 16.0%, meanwhile, the rate of finished sinter, the output of finished sinter and the tumbling index are increased by 2.03%, 7.0% and 3.71% , respectively, with incorporating 0.2% of additive ZC 1 in the sintering mixture, which is in agreement with the catalyzing mechanism of ZC 1.
The mechanism of additive ZC 1 for catalyzing combustion of coke breeze in sintering of iron ore fines was studied by using X ray Diffraction, TGA and GC (Gas Chromatographer), by which energy saving was achieved on sinter pot test. The results show that the distance between cleavage planes is enlarged and the π electrons are re distributed because of insertion of cations / molecules of ZC 1 into the cleavage planes of carbon, resulting in the weakening of CC bond, improving the adsorption of oxygen and lowering the activation energy of The gasification of carbon from 25.8 kJ / mol to 18.9 kJ / mol, and the burning rate being increased and combustion residual reduced, all of which can lead to lower solid fuel consumption. Compared with additives, the solid fuel consumption is reduced by 16.0%, meanwhile, the rate of finished sinter, the output of finished sinter and the tumbling index are increased by 2.03%, 7.0% and 3.71%, respectively, w ith incorporating 0.2% of additive ZC 1 in the sintering mixture, which is in agreement with the catalyzing mechanism of ZC 1.