【摘 要】
：
本文用高温X射线粉末衍射法研究了成分为(重量百分比)62Fe-23Cr-15Co的可加工永磁合金热处理条件与晶体结构的关系。对高温淬火后只经过时效的样品,以及经过淬火、磁场热处理
【机 构】
：
中国科学院物理研究所,中国科学院物理研究所,中国科学院物理研究所,中国科学院物理研究所,中国科学院物理研究所
论文部分内容阅读
本文用高温X射线粉末衍射法研究了成分为(重量百分比)62Fe-23Cr-15Co的可加工永磁合金热处理条件与晶体结构的关系。对高温淬火后只经过时效的样品,以及经过淬火、磁场热处理和时效的样品摄取了高温德拜·谢乐相,观察了高温相变的差异,测量了时效样品点阵常数随温度的变化。我们发现:只经过淬火和时效的样品在610℃左右出现一新的过渡相(X相)。
In this paper, high temperature X-ray powder diffraction method was used to study the composition of the (percentage by weight) 62Fe-23Cr-15Co machinable permanent magnet alloy heat treatment conditions and the relationship between the crystal structure. The high temperature Debye Sherlocks was taken from the samples after aging only after aging, and after quenching, magnetic field heat treatment and aging. The difference of high temperature transformation was observed and the lattice constant of aging samples was measured with temperature. We found that a new transition phase (phase X) appears at about 610 ° C only for the quenched and aged samples.
其他文献
采用热等静压加工工艺可以提高陶瓷和金属铸件的质量。 采用热等静压技术可以使陶瓷部件具有优异的性能。对烧结陶瓷或压制粉末毛坯在高温-高压下反复进行处理就可去掉材料
本文综述了TM—M型快冷非晶磁性合金的局域原子结构。作为化学短程序的必然结果,在TM原子百分数相对于理想的化学正分成份出现过剩时,将导致TM原子的群集。这一群集有可能给
发明的要点在室温化学镀镍的方法中,最初镀槽中含有:(a)镍盐,(b)次磷酸钠,(c)焦磷酸钠,(d)氢氧化胺。根据所需要的电镀速度来选择氢氧化胺的浓度,以便调节镀槽中的pH达到初
本文报导了在混合稀土金属(Mm)及富镧稀土金属(Ml)为吸氢元素的AB_6型贮氢金属中加入Mn、Al元素部分置Ni,组成MmNi_(5-X)M_X(M:Mn、Al;X:0.25、0.5、0.75、1.0)和MlNi_(3-X)M
本文讨论了太阳能收集器可选用的各种涂层及其真空沉积方法。对大规模生产的涂层成本作了经济分析。
This article discusses the various coatings that can be used with
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
<正> 一、前言 参加营业运输的货车总是处于装车、重车走行及中转、卸车、空车走行及中转、装车的循环之中。为了充分发挥现有运用货车的作用,提高货车使用效率,我国铁路采用
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
我今年十四岁,是一个很平凡的女孩。不高不矮,不胖不瘦,学习努力的话,偶尔可以考到全班第一,懈怠了有时也会在二十名左右徘徊。学数学脑子不太灵光,幸而擅长语文和写作。老师
这是一个关于四位母亲的真实故事。有这么两位母亲,都是养母,都遭遇了不幸——第一位母亲,丈夫出车祸身亡,自己得了尿毒症,在被告知生命大限将至的时候,她没有为自己流泪,却