【摘 要】
：
在ZL102中加入纯Zn、纯Mg,得到Al-12.4Si-4.5Cu及Al-25Zn-10Si-5Mg合金,研究了挤压铸造成形合金的性能。结果表明,两组合金的最佳工艺方案相同,即模具预热温度为240℃,压力为
论文部分内容阅读
在ZL102中加入纯Zn、纯Mg,得到Al-12.4Si-4.5Cu及Al-25Zn-10Si-5Mg合金,研究了挤压铸造成形合金的性能。结果表明,两组合金的最佳工艺方案相同,即模具预热温度为240℃,压力为150kN,保压时间为16s,浇注温度为630℃;挤压铸造件经过淬火时效处理之后,微观组织比未经热处理的微观组织均匀、细小,且硬度明显提高。加入5%的Mg元素后,合金组织性能优于不加Mg的。
Pure Zinc and Pure Mg were added to ZL102 to obtain Al-12.4Si-4.5Cu and Al-25Zn-10Si-5Mg alloys. The properties of extrusion casting alloy were studied. The results show that the optimum process scheme of the two alloys is the same, that is, the mold preheating temperature is 240 ℃, the pressure is 150kN, the dwell time is 16s and the pouring temperature is 630 ℃. After quenching and tempering, the microstructure Compared with the microstructure without heat treatment even, small, and significantly increased hardness. After adding 5% Mg element, the microstructure and properties of the alloy are better than those without Mg.
其他文献
春节热热闹闹地过完了。花卉市场也平静了下来。今年的年宵市场应该没让大家失望,虽然没有太多的新品种,但红火的销售场面仍旧让人鼓舞。说起这个春节我印象最深的花卉品种却
采用双极脉冲磁控溅射法以石墨为靶材在FTO玻璃上制备染料敏化太阳电池(DSSCs)碳对电极.研究衬底温度对碳膜的结构及性能的影响.用四探针测试仪对碳膜的方块电阻进行测试,拉
采用真空感应熔炼技术制备不同B含量的高W、Cr镍基高温合金,测定了合金的持久性能和力学性能,研究了B含量对合金的持久性能和拉伸力学性能的影响。采用SEM和XRD对合金进行了
介绍了运用可熔金属芯,采用砂型铸造方法铸造纯Cu氧枪喷头的工艺方案。针对180mm的3孔氧枪喷头的铸造成形工艺进行了设计,包括工艺流程、可熔金属芯制备、工艺参数的设计,
B-50(GAP-43)蛋白是一种神经生长相关蛋白,对于神经发育、外周神经损伤后再生及突触可塑性等过程有重要意义。本组曾报道损伤大鼠尾壳核后B-50 mRNA呈高表达。为探讨生理条
目的 观察中西药结合治疗痤疮的临床疗效.方法 将169例痤疮患者按治疗方法不同分为中西药结合治疗组(86例)和西药治疗组(83例).2组均治疗1个月后判定疗效.结果 中西药结合治疗组总有效率为88.1%,而西药治疗组总有效率为64.9%,2组比较差异有统计学意义(P＜0.01).结论 中西药结合治疗痤疮疗效优于西药治疗。
早产儿是指胎龄超过28周而未满37周,出生体重低于2500g的活产新生儿.由于早产儿胎龄不足,各器官发育尚未成熟,功能低下,生活能力弱,容易感染疾病,而且病情很快由轻转重导致死
在本能晶粒细化基础上,向高纯Mg-3Al合金熔体中添加Fe元素,对粗化后的晶粒进行碳质孕育法晶粒细化处理,研究了合金凝固后的晶粒尺寸变化,并对Fe的影响机理进行分析与讨论。结
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
以AZ91D镁合金为研究对象,借助X射线衍射仪、金相显微镜、扫描电镜及电化学工作站,研究了在1GPa压力下,时效时间对AZ91D镁合金组织及耐腐蚀性能的影响。结果表明,随着时效时