本文研究了0.032wt％和0.069wt％Zr的加入对经92％冷拔变形、直径为2.87mm的导电用工业纯铝线材的再结晶温度和恒温下的再结晶动力学的影响。
In this paper, the effects of the addition of 0.032wt% Zr and 0.069wt% Zr on the recrystallization temperature and the recrystallization kinetics at a constant temperature of 92% cold-drawn, 2.87mm diameter commercial pure aluminum wire were studied.