【摘 要】
：
The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed
【机 构】
：
School of Metallurgical and Ecological Engineering,Office of the Chinese Society of Rare Earths,Nati
论文部分内容阅读
The nano powders of LaCrO3 were prepared by a sol-gel route. The heat capacity of LaCrO3 nano powders from 350 to 550 K was measured by DSC method and expressed as: Cp(LaCro3) (±0.112) = 166.844 - 8.500 × 10-3T - 1.022 ×vanic cell. From measured EMF data of the reversible cell, (-) Pt, La2O3, LaF3, O2 (1 atm)|CaF2|O2(1 atm), LaF3, LaCrO3, Cr2O3, Pt(+), and the relevant value of Gibbs free energy, the Gibbs free energy of formation of LaCrO3 was calculated from 700 to 885 K: △G(φ) f,LaCro3 = -1555.364 + 0.354T (kJ/mol) (700-885 K). And the Gibbs free energy change of reaction from simple oxides La2O3 and Cr2O3 was calculated to be: △G(φ) f,ox(LaCrO3) = -94.758 + 8.530 × 10-2T (kJ/mol) (700-885 K).
其他文献
报道了乙炔银与可溶性银盐形成复盐的合成过程,研究了C2-2在复盐里的配位方式和C2-2的Raman光谱,讨论了C2-2阴离子的配位化学与等电体N2分子在固氮中心FeMoco里的结合方式的
以电化学原位时间分辨FTIR反射光谱和循环伏安方法研究甲酸在不同Sb覆盖度修饰的Pt(100)单晶电极上的氧化.发现Sbad的修饰抑制了甲酸的解离吸附,使反应经活性中间体直接氧化
利用作者自行开发和改良的MonteCarlo计算机仿真算法，对含不同数量第二相粒子的虚拟材料基体中三维晶粒长大过程的影响进行了仿真和定量分析结果表明，随粒子体积分数增加，晶粒长
本文开展了红外辐射材料ZrO2、Al2O3及其复合氧化物ZrO2-Al2O3的纳米材料制备方法研究,对其开展了FTIR,NIR FT-Raman、XRD和红外发射光谱研究,研究表明复合氧化物具有较好的
用DTA和XRD研究了LiNiO2在空气中的热分解过程为：LiNiO2(s)650～720℃ Li2Ni8O10(s)+4Li2O(s)+ O2(g)850～950℃Li2O(s)+8NiO(s)+1／2 O2(g)1000～1150℃NiO(s)+Li2 O(g)用Doyle-Ozawa
通过振动光谱和X-射线结构分析数据的结合,归属了系列具有[M3YS3M′](M＝Mo,W;Y＝O,S;M′＝Cu,Sn,Sb,Pb,Bi)簇芯的异金属四核类立方烷原子簇化合物的主要振动谱峰.讨论了五种结构类
合成了一系列单立方烷M-Fe-Se和M-Cu(Ag)-S(Se)簇合物,并用UV,IR和X-光衍射等方法对上述簇合物进行了分析。
在磷酸系晶型控制剂的作用下,通过氢氧化钙悬浊液的非均相沉淀法合成了文石型晶须,研究了在此方法中晶型控制剂、温度以及初始pH值等工艺因素对文石生长的影响规律.利用粉末X
通过2,2′-联吡啶取代的草酸铬化合物和氯化钆在水溶液中反应合成了草酸根桥联的钆-铬六核双金属配合物的晶体.本文着重讨论该配合物的红外光谱。
采用铜蒸气脉冲激光光源和时间分辨探测技术,实现了对JY U1000拉曼光谱仪的高温改造,可在样品温度高至2 023 K下稳定地测谱;二硅酸钠晶体、玻璃及其熔体的测量结果表明,高温R