【摘 要】
：
以乙酸锌为锌源,乙二醇和水为溶剂,采用溶剂热法制备纳米氧化锌(ZnO),对其制备过程中的影响因素进行研究。利用SEM、XRD等测试手段对催化材料进行表征分析。结果表明,当溶剂
【机 构】
：
郑州师范学院化学化工学院,许昌学院化学化工学院,许昌学院学报编辑部,
论文部分内容阅读
以乙酸锌为锌源,乙二醇和水为溶剂,采用溶剂热法制备纳米氧化锌(ZnO),对其制备过程中的影响因素进行研究。利用SEM、XRD等测试手段对催化材料进行表征分析。结果表明,当溶剂热温度为140℃时,催化活性最高,紫外光照5h后,亚甲基蓝的降解率达到92%。纳米ZnO主要是由纳米棒组成的微球体,其平均晶粒半径约为56.4nm。
Zinc acetate was used as zinc source, ethylene glycol and water as solvent, and ZnO was prepared by solvothermal method. The influencing factors in the preparation of ZnO were studied. The catalytic materials were characterized by SEM, XRD and other means. The results showed that when the solvothermal temperature was 140 ℃, the catalytic activity was the highest, and the degradation rate of methylene blue reached 92% after UV irradiation for 5h. Nanometer ZnO is mainly composed of nanorods microspheres, the average grain radius of about 56.4nm.
其他文献
通过恒电压以及脉冲电压在直接甲醇燃料电池(DMFCs)阳极催化剂载体(垂直取向石墨烯)表面电沉积Pt。对制得的催化剂采用扫描电子显微镜、透射电子显微镜、拉曼光谱仪、X射线衍
介孔SiO2(MSN)在药物输送、酶固定和催化等领域有广泛的应用。由于MSN极易团聚,使其应用受到限制。接枝改性能有效地改善这一缺点,接枝改性包括小分子改性和聚合物改性。主要
小学数学教学活动要关注小学生的学习需求,创设有效的问题情境,发挥学生在学习过程中的创造性、实践性和主动性.本文深入探讨和分析小学数学问题情境创设需要重视和关注的方
“兴趣是学生最好的老师”,因此教师在教学过程中应将培养学生学习兴趣放在首位.在小学英语课堂中教师采用新颖的游戏教学,既符合小学生的心理特征,又极大地激发了学生的学习
由于锂空气电池有很高的理论能量密度,受到了研究人员的广泛关注。该种电池使用纯金属锂作为负极,正极为氧气,不需要在电极中储存,直接来自空气中。然而锂氧电池在实际应用中
在新课程改革理念的指导和支持下,在化学实验教学中教师不仅要向学生传授相应的化学知识,也应该加强对学生自学能力的培养,力求将学生培养成为高素质人才.本文从微课教学入手
小学语文识字和阅读是语文教学的两大亮点,亦是学生获取知识的重要渠道,在小学语文教学中开展识字教学和阅读教学不仅可以为小学生后续的学习打下良好基础,同时良好的阅读习
制备了磷钨杂多酸离子液体[BMIM]_3PW_(12)O_(40)、[BMIM]_3PMo_(12)O_(40)和[MIMPS]_3PW_(12)O_(40),以它们为催化剂,分别以离子液体[BMIM]PF_6和[BMIM]BF_4为萃取剂,30%H_2O_2为氧化剂,考察了不同脱硫体系对模拟汽油中二苯并噻吩(DBT)的脱除效果。其中,在催化氧化萃取耦合脱硫体系[MIMPS]_3PW_(12)O_
采用水热法,在FTO衬底上生长纳米棒状结构,进一步SEM分析,TiO2纳米棒状结构的周围及尖端由花状结构组成。将这种结构与镀金的FTO衬底组装成探测器,在紫外光照下的光电流密度