【摘 要】
：
研究了Ni60、Al2O3+40%TiO2及Ni/Al2O3涂层的摩擦磨损性能,并与T10钢的耐磨性进行了比较,探讨了涂层的磨损机制.实验表明,Ni60涂层耐磨性最好,在低载荷下,涂层失效是由表面接
【机 构】
：
河北工业大学材料科学与工程学院,河北工业大学材料科学与工程学院,河北工业大学材料科学与工程学院,河北工业大学材料科学与工程学院,河北工业大学材料科学与工程学院,河北工业大学材料科学与工程学院,河北工业
论文部分内容阅读
研究了Ni60、Al2O3+40%TiO2及Ni/Al2O3涂层的摩擦磨损性能,并与T10钢的耐磨性进行了比较,探讨了涂层的磨损机制.实验表明,Ni60涂层耐磨性最好,在低载荷下,涂层失效是由表面接触疲劳引起的;在高载荷下,由于涂层颗粒剥落产生了磨粒磨损.Al2O3+40%TiO2涂层由于陶瓷脆性大,在磨损过程中产生脆断,并且随脆性增加,由脆断引起的磨损量增加.
The friction and wear properties of Ni60, Al2O3 + 40% TiO2 and Ni / Al2O3 coatings were studied and compared with the wear resistance of T10 steel.The wear mechanism of the coating was discussed.The results show that the wear resistance of Ni60 coating is the highest Good, under low load, the coating failure is caused by the surface contact fatigue; under high load, due to the coating particles spalling abrasive wear.Al2O3 + 40% TiO2 coating due to ceramic brittleness in the wear process Produce brittle fracture, and increase with the brittleness, the amount of wear caused by brittle fracture increases.
其他文献
为了研究燃料成分变化对超燃冲压发动机燃烧特性的影响,以气化RP-3(中国3#航空煤油)和乙烯为燃料进行了一系列直连式燃烧试验。模型燃烧室入口参数为Ma=2.92,3.46,总温Tt=143
根据氯丁橡胶在空气、海水中的老化实验结果,用非线性回归法处理数据,分别计算了该橡胶在海水和空气中的老化动力学参数.结果表明,在相同温度条件下,橡胶在海水中比在空气中
目的探索转子间骨折内固定物的合理应用。方法采用目前常用的内固定物Gamma钉与Richard治疗转子间骨折48例,其中Gamma钉17例,Richard钉31例,进行临床比较、力学分析。结果稳
在成熟的市场，兼并、收购和整合将可能是2014这一年市场重组的实质性表征。这些变化在某些市场会远远超越简单的买卖电信资产，而是代表着市场份额和主要参与者之间总体平衡的重
<正> 几个世纪以来,许多科学家对生物寿命作了大量的探究,发现动物中以海龟最为长寿,能活到一千多年;植物中则以针叶松的寿命为最长。最近在美国的加利福尼亚州,发现一种高达
慢性咳嗽在经过严格的诊断程序后仍有约10%的患者病因未明,难以进行针对性的西医治疗,这正是发挥中医辨证论治优势的领域。本研究针对慢性咳嗽不明原因病例的临床症状及中医
为深入探索城镇化空间推进的过程及其特征,利用顺义区1992、1999和2009年3期遥感土地利用/覆盖解译数据,采用土地利用动态度和土地利用变化空间分析模型,以及土地利用空间变
<正>为贯彻实施《特殊医学用途配方食品注册管理办法》,保障特殊医学用途配方食品市场供应,国家食品药品监督管理总局联合国家质量监督检验检疫总局发布关于调整特殊医学用途
目的:对脑卒中偏瘫患者进行针灸、中频电加高压氧早期综合康复治疗的效果观察。方法:将67例脑卒中患者分为两组,对照组行头颅CT或MRI检查,给予神经科常规药物治疗,康复组行头
文章对中美两国高等教育信息化建设的基本情况和两国教育信息化存在的问题进行了比较研究,总结出对我国高校教育信息化建设的启示,以期能够促进我国高校教育信息化的发展。