【摘 要】
：
许多高光洁度(▽10～▽11)钢质零件表面(特别是平面和球面),例如飞机柱塞式油泵转子和分油器配流面,柱塞头和万向接头球面等,研磨后经常发现肉眼可见的凹坑,呈黑色,生产中称为
论文部分内容阅读
许多高光洁度(▽10～▽11)钢质零件表面(特别是平面和球面),例如飞机柱塞式油泵转子和分油器配流面,柱塞头和万向接头球面等,研磨后经常发现肉眼可见的凹坑,呈黑色,生产中称为黑点。黑点一般深1～1.5微米,少数达60微米;横向尺寸30～60微米,个别达100微米。这在低光度(▽9以下)下或不仔细观察时难以看到,但
Many high-quality (▽ 10 ~ ▽ 11) steel parts surface (especially the plane and spherical), such as aircraft piston pump rotor and splitter flow surface, plunger head and universal joint spherical, often found after grinding Pits visible to the naked eye, black, known as black spots in production. Dark spots generally 1 to 1.5 microns deep, a few up to 60 microns; horizontal size of 30 to 60 microns, each up to 100 microns. This is difficult to see under low light (below ▽ 9) or without careful observation, however
其他文献
本文初步研究了影响20Mn2[注一]焊接元环链疲劳寿命的因素,并采用喷丸强化使焊接元环链疲劳寿命达到国家C级标准(即国际C级)。
In this paper, the factors influencing the
高铬铸钢做为轧钢导板材料,其使用寿命比铸铁导板高500倍以上,为了弄清这种材料的耐磨机理,应首先了解这种钢在铸态及其经轧制3000吨钢后的组织结构。一、铸钢的相鉴定高铬
本试验以单、双辊装置激冷Al—Cu系合金,研究了冷速与组织的关系,探讨了把竞争生长理论运用到高速激冷中去的可能性,并把定向凝固获得的λ~2R=const结论推广到激冷凝固中,所
本文合成了十三种镧系离子(La,Pr,Nd,Sm,~-Eu～Lu)与1—苯基—3—甲基—4—苯甲酰基—5—呲哇啉酮(HPMBP)和邻菲啰镧(phen)形成的三元混配配合物.元素分析确定其组成为 Ln(PMBP
无铬8号钢是立足于我国资源而研制成功的一种高压锅炉过热器管用钢。为了促进无铬8号钢的应用,进行了研制供该钢焊接用的焊条和焊丝的工作。目前研制成功的焊条(或焊丝),与相
焊炬和割炬按乙炔与氧气混合的方式不同,可分为射吸式和等压式两种。目前国内生产的焊炬和割炬是射吸式的,而且是分别制造生产,分别单独使用,因此适用范围比较小。射吸式焊
本文用Hha I DNA甲基化酶为工具酶,制备了甲基化水平为2.39％的Micrococcus luteus DNA(天然的M.L.DNA是完全未甲基化的)。又以CD光谱、UV光谱及微量热法等手段,比较了甲基化和
CA10B和CA30B汽车共有圆柱形弹簧137种,需要磨端面的有25种,如图1。按φ的大小分为: 第一类,φ=7.0～7.5叫大弹簧,如120—3514045;第二类,φ=3.75叫中弹簧,如120—1007020;第
这种新的镜面加工方法能以小的压力获得近十倍于精密磨削的去除效率,约10μR_z(R_z 为十点平均表面粗糙度)的预加工面经加工几分钟后就能达到0.1μR_z,用很细的磨料容易获得
外圆法(CBMS)的二个重要的研究课题是:最大程度地提高平均淬火速率及控制非晶带的尺度.本文从粘性流体动力学方程组出发,求得溶潭内涡旋?(图4)、速度矢量?及温度T(图5)的分