论文部分内容阅读
Manganese oxides supported by ZSM-5 zeolite (Mn/ZSM-5) as well as their further modified by Ce promoter were achieved by simple impregnation method for ozone catalytic decomposition.The yCe20Mr/ZSM-5-81 catalyst with 8％ Ce loading showed the highest catalytic activity at relative humidity of 50％ and a space velocity of 360 L/(g × hr),giving 93％ conversion of 600 ppm O3 after 5 hr.Moreover,this sample still maintained highly activity and stability in humid air with 50％-70％ relative humidity.Series of physicochemical characterization including X-ray diffraction,temperature-programmed technology (NH3-TPD and H2-TPR),X-ray photoelectron spectroscopy and oxygen isotopic exchange were introduced to disclose the structure-performance relationship.The results indicated that moderate Si/Al ratio (81) of zeolite support was beneficial for ozone decomposition owing to the synergies of acidity and hydrophobicity.Furthermore,compared with 20Mn/ZSM-5-81,Ce doping could enhance the amount of low valance manganese (such as Mn2+ and Mn3+).Besides,the Ce3+/Ce4+ ratio of 8Ce20Mn/ZSM-5-81 sample was higher than that of 4Ce20Mn/ZSM-5-81.Additionally,the synergy between the MnOx and CeO2 could easily transfer electron via the redox cycle,thus resulting in an increased reducibility at low temperatures and high concentration of surface oxygen.This study provides important insights to the utilization of porous zeolite with high surface area to disperse active component of manganese for ozone decomposition.