【摘 要】
：
我厂在生产中发现热镀锌后黑心可锻铸铁金具成批变灰变脆,又发现退火后毛坯中亦有灰脆出现。经过理化分析,证明前者系由于镀件在危险温度区间(即低于590℃的锌液中)进行热镀
论文部分内容阅读
我厂在生产中发现热镀锌后黑心可锻铸铁金具成批变灰变脆,又发现退火后毛坯中亦有灰脆出现。经过理化分析,证明前者系由于镀件在危险温度区间(即低于590℃的锌液中)进行热镀锌时产生“回火脆性”的结果;后者系由部分含磷偏高(＞0．19%)的铸件在退火第二阶段保温后冷却速度较慢所致。为了防止和消除上述严重的内在缺陷,保证产品质量,我
I found in the production plant after the hot-dip galvanized malleable cast iron with a batch of ash to become brittle, but also found that the rough blank after annealing there. After physical and chemical analysis, it was proved that the former produced “temper brittleness” when hot-dip galvanized due to plating in dangerous temperature range (ie, zinc solution below 590 ℃); the latter was caused by partial high phosphorus content (> 0.19%) of the castings in the second phase of the annealing after cooling due to the slow cooling. In order to prevent and eliminate the above serious internal defects, to ensure product quality, I
其他文献
本文主要介绍了乌池坝隧道通风竖井二衬施工技术,重点介绍了二衬浇筑模板-整体液压金属模板和改进型输料导管在乌池坝隧道通风竖井二衬施工的应用。
This paper mainly intr
目的观察导管血栓抽吸联合冠脉支架置入治疗急性心肌梗死(AMI)疗效。方法对122例AMI冠脉支架置入治疗病人中的43例急性ST段抬高型AMI(STEMI)患者常规进行冠脉造影术后,确定梗
一、目的与意义 目前板料冲压保持架,广泛采用条料单排或双排交叉冲裁。除部分浪形保持架利用料芯连续套裁以外,其他绝大部分料芯都未利用或未充分利用,材料实际利用率约为2
离去训练馆还有一刻钟,队友们有的还在洗漱、整理内务,陈中却早已收拾妥当躺在床上看书,她说这是一种习惯。她看的是一本情感类杂志,远望去都是密密的字,如果不知道她是陈中,
微区域X光光谱仪,又名电子探针X射线显微分析仪(Electron probe x-ray microanalyzer),是近十年来才发展起来的一种高级精密仪器(图1)。此仪器能分析大多数的固体试样,特别
电位溶出法用于分析可溶于汞的金属时,与阳极溶出伏安法有相近的灵敏度,仪器较简单。当用玻碳汞膜电极时,常以二价汞离子或溶液中溶解的氧为氧化剂。D.Jagner在玻碳电极上以
本文是介绍退火对海绵钛机械性质影响的实验研究情况。研究结果表明,按现行技术条件规定在700℃下进行退火不能正确反映出海绵钛的质量。但在920～950℃下进行退火,然后试样与
车床床身导轨和配研溜板纵向导轨大修以后,必然引起溜板和溜板箱的下沉,也就是:造成絲杠、光杠的中心线高于溜板箱开合螺母、光杠滑套中心线以及齿条节线高于溜板箱纵走刀齿
过去这一年多来,明尼苏达森林狼队陆续清出了加内特(Kevin Garnett)、R.戴维斯(Ricky Davis)、布朗特(Mark Blount)、沃克(Antoine Walker)、贾里奇(Marko Jaric)、格林(Gera
将一项运动浸渍在白色理念中,是因为它给人一种内敛恬淡的感觉,更多的还在于它能让练习者处在平静、安详但又不乏灵动的境界里。这种运动让人感到些许遥远,可是一旦“潜入”