Spinel (MgAl2O4) ultrafiltration membranes were prepared on porous α-Al2O3 plates via the sol-gel route. Mg-Al double alkoxide [MgAl2(iprO)s] was first synthesized as the precursor, then hydrolyzed and peptized in aqueous solution. The gel layer was coated from the colloidal sol on the intermediate layer (α-Al2O3), which was formerly prepared to modify the porous substrate, and then thermally treated at 900℃. The processing parameters such as pH, temperature and sol composition during the sol preparation were optimized for controlling particle size. The pore size of the 2μm thick top layer is about 13 nm as estimated by both the BSA (Bovine Serum Albumin)retention test and an empirical equation.The water permeability of the obtained spinel membrane is 55～143 kg/(min.cm2.Pa).