A composite hard-anodized coating containing micro PTFE (polytetrafluoroethylene) particles on aluminum alloy 6063 was produced by adding micro PTFE particles into the traditional hardcoat anodizing solution. The size of the PTFE particles is around 2 v- m in diameter and the content of the PTFE particles in the composite coating is within 2%-3% by area percentage. Thickness of the composite coating can reach up to 70 v m after one hour’s anodizing. Surface hardness of the composite coating is between 400-480 HVo.i- The average friction coefficient of the composite coating against steel under dry friction test is 0.11, which is 17% lower than that obtained by traditional hardcoat anodizing.
A composite hard-anodized coating containing micro PTFE (polytetrafluoroethylene) particles on aluminum alloy 6063 was produced by adding micro PTFE particles into the traditional hardcoat anodizing solution. The size of the PTFE particles is around 2 v-m in diameter and the content of the PTFE particles in the composite coating is within 2% -3% by area percentage. Thickness of the composite coating can reach up to 70 vm after one hour’s anodizing. Surface hardness of the composite coating is between 400-480 HVo.i- The average friction coefficient of the composite coating against steel under dry friction test is 0.11, which is 17% lower than that obtained by traditional hardcoat anodizing.