To explore the preparation of porous nickel–titanium alloy with excellent properties, larger size and complex shape, the premixed powder of Ni and Ti with atomic ratio of 1:1 was shaped by gel-casting. The effects of solids loading and the content of dispersant on flow ability of nickel–titanium slurry and the mechanical properties of nickel–titanium sintered body were studied. The drying models under different solids loading were also discussed.The results show that the viscosity of slurries significantly increases with an increase in solids loading. After a proper process of drying, the green body with complex shape is obtained. The sintered body with porosity rate reaching up to49.5 % and compression strength reaching to 364.74 MPa could meet the basic demands of implant materials.
To explore the preparation of porous nickel-titanium alloy with excellent properties, larger size and complex shape, the premixed powder of Ni and Ti with atomic ratio of 1: 1 was shaped by gel-casting. The effects of solids loading and the content of dispersant on flow ability of nickel-titanium slurry and the mechanical properties of nickel-titanium sintered body were studied. The drying models under different solids loading were also discussed.The results show that the viscosity of slurries precipitations with an increase in solids loading. After a proper process of drying, the green body with complex shape is obtained. The sintered body with porosity rate reaches up to 49.5% and compression strength reaches 364.74 MPa could meet the basic demands of implant materials.