论文部分内容阅读
In continuous annealing lines/hot galvanizing,strips are guided by upper and lower rolls in an alternate up and down vertical motion.This kind of process consisting of heating,soaking,and cooling furnaces(or zones) has several advantages in terms of productivity and product quality.Main problems encountered in continuous annealing lines are misguiding and formation of buckling.The strip buckling causes the strip to be rejected and,in the worst case,the strip breaks and the continuous annealing lines are compelled to stop.In this paper the elastic-plastic model of the strip traveling and the corresponding boundary condition were constructed dependant on the theory of mechanic.Simulations are performed in two steps.First,a homogeneous longitudinal tensile stress is applied at one end of the strip,the other end of the strip and the roll are restricted.In the second step,the applied tension remains constant.A uniform displacement is applied to the other end of the strip and a rotation to the roll. The transverse compressive stress,the buckling formation during strip traveling process,the location for the buckling taking place and the buckling criterion were investigated systematically.The result shows that the transverse compressive stress increases with the increase of the tensile stress and the crown of the tapered roll. Because the contact area between the tapered roll and the strip increase with the decrease of the crown,the tensile stress distribution is more homogeneous in the transverse direction of the strip.An additional transverse compressive stress is created and a buckling is also observed due to the friction during the strip motion in the second step.Once the buckling is appearance,it is very hard to be removed only through decreasing the applied longitudinal tension,because the strip wrinkle still keeps high level due to the effect of the buckled strip,the wrinkle would evolve into buckling eventually.The buckling formation process predicted by the finite element model is very similar to those observed in industrial processing lines.It takes place on the cylindrical part of the tapped roll and the buckling is moving to the middle part of the tapped roll with the increase of the crown,its width is about 2-4 mm.The criterion for the buckle occurrence is also discussed,in the prescribed situation,the transverse shell curvature increases with the strip displacement,if the transverse shell curvature reaches 0.1 mm~(-1), the buckling would take place.
In Continuous annealing lines / hot galvanizing, strips are guided by upper and lower rolls in an alternate up and down vertical motion. This kind of process consisting of heating, soaking, and cooling furnaces (or zones) has several advantages in terms of productivity and product quality. Problems encountered in continuous annealing lines are misguiding and formation of buckling. The strip buckling causes the strip to be rejected and, in the worst case, the strip breaks and the continuous annealing lines are compelled to stop. In this paper the elastic-plastic model of the strip traveling and the corresponding boundary conditions were constructed dependant on the theory of mechanic. Simulations are performed in two steps. First, a homogeneous longitudinal tensile stress is applied at one end of the strip, the other end of the strip and the roll are restricted.In the second step, the applied tension remains constant. A uniform displacement is applied to the other end of the strip and a rotation to t The transverse compressive stress, the buckling formation during strip traveling process, the location for the buckling taking place and the buckling criterion were systematically. The result shows that the transverse compressive stress increases with the increase of the tensile stress and the crown because of the contact area between the tapered roll and the strip increase with the decrease of the crown, the tensile stress distribution is more homogeneous in the transverse direction of the strip. An additional transverse compressive stress is created and a buckling is also observed due to the friction during the strip motion in the second step. Once the buckling is appearance, it is very hard to be removed only through decreasing the applied longitudinal tension, because the strip wrinkle still keeps high level due to the effect of the buckled strip, the wrinkle would evolve into buckling eventually. The buckling formation process predicted by the finiteelement model is very similar to those observed in industrial processing lines. It takes place on the cylindrical part of the tapped roll and the buckling is moving to the middle part of the tapped roll with the increase of the crown, its width is about 2- 4 mm. The criterion for the buckle occurrence is also discussed, in the prescribed situation, the transverse shell curvature increases with the strip displacement, if the transverse shell curvature reaches 0.1 mm -1, the buckling would take place.