The Role of Surfactant and Costabilizer in Controlling Size of Nanocapsules Containing TEGDMA in Min

• 作 者: 郭进新 黄翠
• 机 构: School and Hospital of Stomatology,Wuhan University,Key Laboratory of Oral Biomedical Engineering of
• 出 处: Journal of Wuhan University of Technology(Materials Science
• 发表日期: 2009年06期
• 关键词: surfactant bonding resin preliminarily glycol polyurethane sizes synthesize inte

Nanocapsules with triethylene glycol dimethacrylate (TEGDMA) as core material and polyurethane as wall material used for self-healing bonding resin were prepared by interfacial polycondensation in miniemulsion. The influence of surfactant and costabilizer concentration on nanocapsules size and stability of nanocapsules was investigated. The size and its polydispersity of the nanocapsules were measured by light-scattering particle size analyzer. When the concentration of SDS were increased from 2.5wt% to 10wt%,the size decreases from 340.5 nm to 258.3 nm, PDI decreased from 0.210 to 0.111. As the concentration of HD increased, the size and PDI were both decreased, When reaching 10wt%,the size was 258.0 nm,PDI was 0.130. SDS and HD play important effect in synthesis of Nanocapsules containing TEGDMA.By changing the surfactant and costabilizer concentration it was possible to synthesize a wide variety of nanocapsules sizes. The performance and technical parameters of nanocapsules had been researched preliminarily, which built the solid foundation for the application to the self-repairing bonding resin.

Nanocapsules with triethylene glycol dimethacrylate (TEGDMA) as core material and polyurethane as wall material used for self-healing bonding resin were prepared by interfacial polycondensation in miniemulsion. The influence of surfactant and costabilizer concentration on nanocapsules size and stability of nanocapsules was investigated. The size and the polydispersity of the nanocapsules were measured by a light-scattering particle size analyzer. When the concentration of SDS were increased from 2.5 wt% to 10 wt%, the size decreases from 340.5 nm to 258.3 nm, PDI decreased from 0.210 to 0.111. As the concentration of HD increased, the size and PDI were both decreased when reaching 10wt%, the size was 258.0nm, PDI was 0.130. SDS and HD play important effect in synthesis of Nanocapsules containing TEGDMA.By changing the surfactant and costabilizer concentration it was possible to synthesize a wide variety of nanocapsules sizes. The performance and technical parameters of nanocapsules had been researched preliminarily, which built the solid foundation for the application to the self-repairing bonding resin.