【摘 要】
：
The microstructure, mechanical and micro/nano-tribological properties of the 60NiTi film annealed at different temperature were investigated. The results reveal that annealing as-deposited 60NiTi film at 300, 375, and 600 ℃ for 1 h leads to structural rel
【机 构】
：
Key Laboratory of Education Ministry for Modern Design and Rotor-Bearing System,Xi’an Jiaotong Unive
论文部分内容阅读
The microstructure, mechanical and micro/nano-tribological properties of the 60NiTi film annealed at different temperature were investigated. The results reveal that annealing as-deposited 60NiTi film at 300, 375, and 600 ℃ for 1 h leads to structural relaxation, partial crystallization and full crystallization, respectively. Compared with the structurally relaxed structure, the partially crystallized structure exhibits increased hardness but decreased elastic modulus. This is because that the elastic modulus is reduced by Voigt model while the hardness is improved by composite effect. Due to the highest hardness and ratio of hardness to elastic modulus (H/E), the partially crystallized 60NiTi film has the lowest penetration depth and residual depth (i.e., groove depth). Besides, the results also reveal that ductile plowing is the dominant wear mechanism for all the annealed 60NiTi films. Under the condition of the ductile plowing, coefficient of friction and wear resistance are related to penetration depth and residual depth, respectively. Therefore, the partially crystallized 60NiTi film shows the best tribological performance at the micro/nano-scale. The current work not only highlights the important roles of hardness and H/E in improving the micro/nano-tribological properties but also concludes an efficient and simple method for simultaneously increasing hardness and H/E.
其他文献
We prepared a graphene/ionic liquid (G/IL) composite material by the hybridization of G and an IL for use as a lubricating oil additive. The friction coefficient and wear volume of a base oil containing 0.04 wt％ of the G/IL composite was reduced by 45％ an
A crosshead slipper-guide system, which bears a significant thrust force, is an essential friction pair in low-speed marine diesel engines. Owing to the low moving speed of the crosshead slipper during engine startup, it is difficult to form good hydrodyn
The tribological characteristics of cotton fibers play an important role in engineering and materials science, and real contact behavior is a significant aspect in the friction behavior of cotton fibers. In this study, the tribological characteristics of
A macroscopically nominal flat surface is rough at the nanoscale level and consists of nanoasperities. Therefore, the frictional properties of the macroscale-level rough surface are determined by the mechanical behaviors of nanoasperity contact pairs unde
Understanding asperity flattening is vital for a reliable macro-scale modeling of friction and wear. In sheet metal forming processes, sheet surface asperities are deformed due to contact forces between the tools and the workpiece. In addition, as the she
The tribological behaviors of Ti–Ni51.5 at％ alloy strengthened by finely dispersed Ni4Ti3 particles in reciprocating sliding against GCr15, Al2O3, and ZrO2 at room temperature were studied. Interestingly, the coefficient of friction (COF) suffered a sheer
Alloys used as bearings in aircraft landing gear are required to reduce friction and wear as well as improve the load-carrying capability due to the increased aircraft weights. Cu–15Ni–8Sn–0.8Nb alloy is well known for possessing good mechanical and wear
Aluminium alloys are commonly used as lightweight materials in the automotive industry. This non-ferrous family of metallic alloys offers a high versatility of properties and designs. To reduce weight and improve safety, high strength-to-weight ratio allo
Sub-surface crack networks in areas of altered microstructure are a common cause for bearing failures. Due to its appearance under light microscopy, the damage pattern is referred to as White Etching Cracks (WEC). The root causes leading to the formation
Thickener formulation plays a significant role in the performance characteristics of grease. The polyurea greases (PUGs) were synthesized using mineral oil (500SN) as the base oil, and by regulating the reaction of diphenylmethane diisocyanate (MDI) and d