An amorphous,colorless,and highly transparent star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized from the poly(ethylene glycol)(PEG),pentaerythritol,and dichloromethane by Williamson reaction.FTIR and ~1H-NMR measurement demonstrated that the polymer repeating units were C[CH_2-OCH_2O-(CH_2CH_2O)_m-CH_2O-(CH_2CH_2O)_n-CH_2O]_4.The polymer host held well mechanical properties for pentaerythritol cross-linking.The gel polymer electrolytes based on Lithium perchlorate(LiClO_4)and ethylene carbonate/propylene carbonate(EC/PC)were prepared and characterized by AC impedance spectroscopy and thermogravimetry(TG),the results showed thermal stability up to at least 150℃and ionic conductivity reaching 8.83×10~(-4)S.cm~(-1)at room temperature.The gel polymer electrolytes were further evaluated in electrochromic devices(ECD) fabricated by transparent PET-ITO and electrochromic active viologen derivative films,and its excellent performance promised the usage of the gel polymer electrolytes as ionic conductor material in ECD.
An amorphous, colorless, and highly transparent star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized from the poly (ethylene glycol) (PEG), pentaerythritol, and dichloromethane by Williamson reaction. FTIR and ~ demonstrated that the polymer repeating units were C [CH 2 -OCH 2 O (CH 2 CH 2 O) _m-CH 2 O (CH 2 CH 2 O) _n-CH 2 O] _4.The polymer host held well mechanical properties for pentaerythritol cross-linking.The gel polymer electrolytes based on Lithium perchlorate (LiClO_4) and ethylene carbonate / propylene carbonate (EC / PC) were prepared and characterized by AC impedance spectroscopy and thermogravimetry (TG), the results showed that thermal stability up to at least 150 ℃ and ionic conductivity reached 8.83 × 10 ~ (-4) ) S.cm ~ (-1) at room temperature. The gel Polymer electrolytes were further evaluated in electrochromic devices (ECD) fabricated by transparent PET-ITO and electrochromic active viologen derivative films, and its excellent performance prom ised the usage of the gel polymer electrolytes as ionic conductor material in ECD.