The analysis of threading dislocation density(TDD)in Ge-on-Si layer is critical for developing lasers,light emitting diodes(LEDs),photodetectors(PDs),modulators,waveguides,metal oxide semiconductor field effect transistors(MOS-FETs),and also the integration of Si-based monolithic photonics.The TDD of Ge epitaxial layer is analyzed by etching or transmission electron microscope(TEM).However,high-resolution x-ray diffraction(HR-XRD)rocking curve provides an optional method to analyze the TDD in Ge layer.The theory model of TDD measurement from rocking curves was first used in zinc-blende semiconductors.In this paper,this method is extended to the case of strained Ge-on-Si layers.The HR-XRD 2θ/ωscan is measured and Ge(004)single crystal rocking curve is utilized to calculate the TDD in strained Ge epitaxial layer.The rocking curve full width at half maximum(FWHM)broadening by incident beam divergence of the instrument,crystal size,and curvature of the crystal specimen is subtracted.The TDDs of samples A and B are calculated to be 1.41×10~8cm~(-2)and 6.47×10~8cm~(-2),respectively.In addition,we believe the TDDs calculated by this method to be the averaged dislocation density in the Ge epitaxial layer.
The analysis of threading dislocation density (TDD) in Ge-on-Si layer is critical for developing lasers, light emitting diodes (LEDs), photodetectors (PDs), modulators, waveguides, metal oxide semiconductor field effect transistors and also the integration of Si-based monolithic photonics.The TDD of Ge epitaxial layer is analyzed by etching or transmission electron microscope (TEM) .However, high-resolution x-ray diffraction (HR-XRD) rocking curve provides an optional method to analyze the TDD in Ge layer. The theory model of TDD measurement from rocking curves was first used in zinc-blende semiconductors. In this paper, this method is extended to the case of strained Ge-on-Si layers. The HR-XRD 2θ / ωscan is measured and Ge (004) single crystal rocking curve is utilized to calculate the TDD in strained Ge epitaxial layer. rocking curve full width at half maximum (FWHM) broadening by incident beam divergence of the instrument, crystal size, and curvature of the crystal specimen is subtracted TDDs of samples A and B were calculated to be 1.41 × 10 ~ 8cm -2 and 6.47 × 10 ~ 8cm -2, respectively. In addition, we believe the TDDs calculated by this method to be the averaged dislocation density in the Ge epitaxial layer.