Fe40Ni40P14B6 bulk metallic glass rods have been prepared by water quenching the fluxed alloy. The deformation behavior was investigated by nanoindentation tests and compressing tests. The average hardness and elastic modulus of the as-prepared Fe40Ni40P14B6 BMG (bulk metallic glass) measured by nanoindentation tests are 8.347 and 176.61 GPa respectively. The displace- ment-load curve shows “pop-in” characteristics which correspond to the loading rate bursts. Many shear bands around the indent were observed. The as-prepared Fe-based BMG exhibits a compressive plastic strain of 5.21%, which is much larger than that of other Fe-based glassy alloys and most of other BMGs.
The deformation behavior was investigated by nanoindentation tests and compressing tests. The average hardness and elastic modulus of the as-prepared Fe40Ni40P14B6 BMG (bulk metallic glass) measured by nanoindentation tests are 8.347 and 176.61 GPa respectively. The displace ment-load curve shows “pop-in” characteristics which correspond to the loading rate bursts. Many shear bands around the indent were observed. The as-prepared Fe-based BMG exhibits a compressive plastic strain of 5.21%, which is much larger than that of other Fe-based glassy alloys and most of other BMGs.