In order to control the CaO-Al_2O_3-SiO_2-MgO system inclusions in 50 CrVA spring steel in a lower melting temperature region,high temperature equilibrium experiments between steel and slag were performed in the laboratory,under the conditions of the initial slag basicity within 3-7and the content of Al_2O_3 between 18-35mass%,to investigate the formation and evolution of this type of inclusion.The results indicate that the total oxygen content in the steel decreases with the increase of slag basicity and the decrease of Al_2O_3 content in slags,and CaO-Al_2O_3-SiO2-MgO inclusions tend to deviate from the low melting point region with the increase of Al_2O_3 content in slags.The most favorable composition for the refining slag is composed of 51-56mass% CaO,9-13mass% SiO_2,20-25mass% Al_2O_3 and 6mass% MgO.In this case,the inclusions in 50 CrVA spring steel are mostly in the low melting point regions,in which their plasticities are expected to improve during steel rolling.The MgO-based inclusions were observed in the steel matrix and the formation mechanism was theoretically and schematically revealed.It is also found that adding around 11mass% of MgO into the refining slags is beneficial to reducing the refractory corrosion.Further work should be carried out focusing on the evolution rates of MgO-based inclusions.
In order to control the CaO-Al_2O_3-SiO_2-MgO system inclusions in 50 CrVA spring steel in a lower melting temperature region, high temperature equilibrium experiments between steel and slag were performed in the laboratory, under the conditions of the initial slag basicity within 3 -7and the content of Al_2O_3 between 18-35mass%, to investigate the formation and evolution of this type of inclusion.The results that that total oxygen content in the steel decreases with the increase of slag basicity and the decrease of Al_2O_3 content in slags , and CaO-Al 2 O 3 -SiO 2 -MgO inclusions tend to deviate from the low melting point region with the increase of Al 2 O 3 content in slags. The most favorable composition for the refining slag is composed of 51-56 mass% CaO, 9-13 mass% SiO 2 , 20-25mass% Al_2O_3 and 6mass% MgO.In this case, the inclusions in 50CVA spring steel are mostly in the low melting point regions, in which their plasticities are expected to improve during steel rolling. The MgO-based inclusions were observed in the steel matrix and the formation mechanism was theoretically and schematically revealed. It is also found that adding about 11mass% of MgO into the refining slags is beneficial to reducing the refractory corrosion. Future work should be carried out focusing on the evolution rates of MgO-based inclusions.