【摘 要】
：
柴油机上的油泵彈簧是个很重要的另件。它是用3公厘的鋼絲(俗称白鋼絲,是經过热处理的,与一般黑鋼丝不同)繞成,彈簧的规格是長30公厘,內徑14公厘,外徑20公厘,成型后經过回火
论文部分内容阅读
柴油机上的油泵彈簧是个很重要的另件。它是用3公厘的鋼絲(俗称白鋼絲,是經过热处理的,与一般黑鋼丝不同)繞成,彈簧的规格是長30公厘,內徑14公厘,外徑20公厘,成型后經过回火处理,并进行24小时全压縮試驗(压力大約是10公斤)。根据質量要求,压縮試驗后彈簧的長度不得小于30~(-0.0(?))公厘,并在以后使用中不許再发生变形。
Pump spring on the diesel engine is a very important piece. It is made of 3 mm wire (commonly known as white steel wire, is heat treated, different from the average black wire), the spring is 30 cm long, 14 mm inside diameter, 20 mm outside diameter, After tempering treatment, and a 24-hour full compression test (pressure is about 10 kg). According to the quality requirements, after the compression test, the length of the spring shall not be less than 30 ~ (-0.0 (?)) Mm, and shall not be deformed in future use.
其他文献
The optical properties of Silicon-doped InGaN and GaN grown on sapphire by MOCVD have been investigated by photoluminescence (PL) method. At room temperature, t
患者,女,62岁,因“腹痛8天,伴腹胀、肛门停止排气排便6天”于2014年7月24日收入我院普外科。患者既往体健,置宫内节育环25年,绝经12年,冠心病病史、胆囊结石病史1年。查体:T
现代化不一定要西化林任君编者注：本文作者林任君为新加坡《联合早报》总编辑，前南洋大学荣誉文学士．从事新闻工作１８年。这篇文章摘录于他１９９５年１１月在“九五世界华文报刊与中华文化传播
用釉砂来造型是民主德国的先进经验。它的主要好处是不须用烘模炉烘干,这样可以节约大量燃料,并提高了产量;同时浇铸出的铸件质量相当好。因此在目前增产节约中意义很大,是各
材料——厶18。規格和用途——M30×1.5,M20×1.5兩种;机用絲錐,二級螺紋精度,一次攻出。氰化前情况——淬火后回火三次,精磨到規定尺寸,硬度Rc62～64。氰化处理的操作 1.氰化
我們受「机械工人」編輯部的委托,試用ДЗ-1型焊料来焊接硬質合金刀片和高速鋼刀片。現在把試用情况介紹如下,供大家学習这篇文章时参考。焊料的配制——按原稿介紹的成分
连续速度测井的累计 t_0(H)值与地震测井观测的 t_0(H)值不一致,二者之差,对于深层来说可达数十毫秒,使做出的合成记录与地震记录的反射层 t_0。值不一致。从而影响解释效果
高速鋼在高温鹽爐里加热,大多数用РПС型輻射高温計而不用鉑-铂铑热电偶测量温度;因为用铂-铂铑热电偶测量,保护管容易被高溫鹽燒坏,以致損坏热电偶本身。但РПС型輻射
一、设计及图纸方面的鑑定 设计图纸方面: 1.图纸来源: 该机床系苏联一九四五年至一九四六年试造成功。本厂试造图纸是由局设计处翻译描绘审核而发厂的,故机构设计新颖,图纸
预防孔斜的措施很多,实践表明,用锋利钻头预防孔斜,既经济,效果又好。现谈一点经验体会。
Preventive measures to prevent holes oblique, practice shows that the use of