Additive Ba(N 3) 2 as a source of nitrogen is heavily doped into the graphite-Fe-based alloy system to grow nitrogendoped diamond crystals under a relatively high pressure (about 6.0 GPa) by employing the temperature gradient method.Gem-grade diamond crystal with a size of around 5 mm and a nitrogen concentration of about 1173 ppm is successfully synthesised for the first time under high pressure and high temperature in a China-type cubic anvil highpressure apparatus.The growth habit of diamond crystal under the environment with high degree of nitrogen doping is investigated.It is found that the morphologies of heavily nitrogen-doped diamond crystals are all of octahedral shape dominated by {111} facets.The effects of temperature and duration on nitrogen concentration and form are explored by infrared absorption spectra.The results indicate that nitrogen impurity is present in diamond predominantly in the dispersed form accompanied by aggregated form,and the aggregated nitrogen concentration in diamond increases with temperature and duration.In addition,it is indicated that nitrogen donors are more easily incorporated into growing crystals at higher temperature.Strains in nitrogen-doped diamond crystal are characterized by micro-Raman spectroscopy.Measurement results demonstrate that the undoped diamond crystals exhibit the compressive stress,whereas diamond crystals heavily doped with the addition of Ba(N 3) 2 display the tensile stress.
Additive Ba (N 3) 2 as a source of nitrogen is heavily doped into the graphite-Fe-based alloy system to grow nitrogendoped diamond crystals under a relatively high pressure (about 6.0 GPa) by employing the temperature gradient method. Gem-grade diamond crystal with a size of around 5 mm and a nitrogen concentration of about 1173 ppm is successfully synthesized for the first time under high pressure and high temperature in a China-type cubic anvil high pressureure apparatus. The growth habit of diamond crystal under the environment with high degree of nitrogen doping is investigated. It is found that the morphologies of heavily nitrogen-doped diamond crystals are all of octahedral shape dominated by {111} facets. The effects of temperature and duration on nitrogen concentration and form are explored by infrared absorption spectra. The results indicate that nitrogen impurity is present in diamond predominantly in the dispersed form accompanied by aggregated form, and the aggregated nitrogen concent ration in diamond increases with temperature and duration.In addition, it is indicated that nitrogen donors are more easily incorporated into growing crystals at higher temperatures. Strains in nitrogen-doped diamond crystals are characterized by micro-Raman spectroscopy. Measurement results demonstrate that the undoped diamond crystals exhibit the compressive stress, in diamond crystals heavily doped with the addition of Ba (N 3) 2 display the tensile stress.