研究了16和B95二种合金的蠕变及淬火和人工时效之间形变处理对蠕变的影响。形变选拉伸6％。蠕变温度为1140-190℃,蠕变应力为10-28Kg/mm~2,研究得出:在选定的条件下,该二种合金
论文部分内容阅读
研究了16和B95二种合金的蠕变及淬火和人工时效之间形变处理对蠕变的影响。形变选拉伸6％。蠕变温度为1140-190℃,蠕变应力为10-28Kg/mm~2,研究得出:在选定的条件下,该二种合金的稳态蠕变规律皆为:形变时效并不改变蠕变规律,只不过改变参数。形变时效处理提高18合金的抗蠕变强度,但使B95合金的抗蠕变强度降低。分析了形变时效对合金高温强度影响的原因。
The creep of 16 and B95 alloys and the effect of deformation treatment between quenching and artificial aging on creep were studied. Deformation selection stretching 6%. The creep temperature is 1140-190 ℃ and the creep stress is 10-28Kg / mm ~ 2. The results show that the steady creep laws of the two alloys under the selected conditions are as follows: the deformation aging does not change Creep law, just change the parameters. Deformation aging treatment increases the creep strength of 18 alloy, but decreases the creep strength of B95 alloy. The reason of the effect of deformation aging on the high temperature strength of the alloy was analyzed.
其他文献
0626041基于FPGA的FIR数字滤波器的设计〔刊,中〕/李星//电子科技.—2006,(7).—16-18,22(D)0626042利用lifting方法设计双正交滤波器组〔刊,中〕/徐小平//纺织高校基础科学
我们知道,广泛应用在电子电器设备中的整流二极管,是一种具备单向导电特性的电子元件,如果我们充分利用这一特性,将二极管串接于各电子电路及电器和日常照明灯具中,那么即可
标题化合物单晶由溶液法合成,呈紫红色,用X—射线衍射法测定了晶体及分子结构。晶体属于三斜晶系,空间群P_(?)(No.2),晶胞参数为a=12.880(4),b=13.649(7),c=21.670(5)(?),α=
为了引弧方便和提高装焊速度、质量,我们自制了一台高频引弧器,其外观见图1。这一台引弧器经一年多的使用,很受工人师傅的欢迎。特别是应用在焊接件的装配点焊中,引弧迅速,
最近时期,国外设计制造了不少综合加工自动线。现就Goss公司制造的一条具有代表性的差速器壳综合加工自动线介绍如下。图1为这条自动线的外观图。自动线完成的加工工艺这条
花县花山工具厂使用的尖嘴钳热压锻模,选用3Cr2W8V 钢制作,硬度要求为HRC46～48,外形尺寸为75×75×105毫米(见图1)。
Huaxian Huashan Tools Factory used needle nose plie
目的评价宫颈内膜外移感染治疗托治疗宫颈炎的临床疗效和安全性。方法自身对照多中心临床研究。结果 6个临床中心共入选患者120例,1例退出,成功完成治疗和随访的119例患者平
姚明怒了。在萨克拉门托的阿科球馆.姚明度过了一个无法忘却的伤心之夜。不但队伍铩羽而归,而且自己还被6次判罚出场。温文尔雅的姚明一直是NBA绅士球员的典范.但这一次.他却
考试可以被看成是一种对于学习结果的测量。谈到任何一种考试，都不可避免地要谈到几个概念：效度（Ｖａｌｉｄｉｔｙ）、信度（Ｒｅｌｉａｂｉｌｉｔｙ）、可操作性（Ｐｒａｃｔｉｃａｌｉｔｙ）和对教学的影响（ＢａｃｋｗａｓｈＥｆｅｃｔ）。在教育测量中，效度是一个...
Exam can be see
随着我国国防工业及工农业的发展,对低温材料的需要日益增多。过去,对于工作温度低于—120℃的设备,均选用铝、铜或不锈钢来制造。我国铬、镍资源暂还比较缺少,迅速扭转在低