【摘 要】
：
Ni0.3Cu0.07Zn0.63Fe2-xLaxO4 ferrites were prepared by solid phase method and sintered at 1,150 ℃ for 6 h.The phase formation,microstructure,and magnetic proper
【机 构】
：
State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Scien
论文部分内容阅读
Ni0.3Cu0.07Zn0.63Fe2-xLaxO4 ferrites were prepared by solid phase method and sintered at 1,150 ℃ for 6 h.The phase formation,microstructure,and magnetic properties of samples were investigated.With doping of La3+,the samples contain two phases:LaFeO3 and NiCuZn ferrites.Scanning electron microscope (SEM) image shows that La doping constrains the growth of NiCuZn ferrite,which is more uniform.La doping improves magnetic properties of NiCuZn ferrite when x ≤ 0.03.The saturation magnetization (Ms) increases first;when x =0.03,the highest value is 75.35 A.m2.kg-1.The permeability increases to the maximum value with frequency and then decreases with the concentration of La3+ increasing.When x =0.03,the maximum value of real permeability at 1 MHz is 333.5,and the loss angle tangent (tanδ) is not more than 0.02.La doping improves the properties of NiCuZn ferrite,which can be applied to low-frequency filters.
其他文献
Propping acts by controlling shareholders are common in Chinese listed firms In this paper, we use data on related-party transactions of all listed Chinese firm
采用激光焊接方法对2 mm厚喷射成形的7055铝合金进行了焊接实验。通过背散射电子衍射技术(EBSD)、扫描电镜(SEM)、能谱仪(EDS)、透射电镜(TEM)、显微硬度和室温拉伸试验等测
采用耦合应力的晶体相场法,研究纳米晶在单向拉伸过程中,大角度晶界和小角度晶界的运动,以及诱发晶体长大机制的联系。结果表明,在单向拉伸过程中,应力诱发了晶体长大,并且存
面对中国文化在近代遭遇的危机，在对斯宾格勒与汤因比文化形态学批判地吸收基础上，朱谦之建立了自身的文化形态学体系，从而在理论上处理了中国文化命运及其未来形态的问题。本文
The band alignment of HfO_2 film on p-type(100) InP substrate grown by magnetron sputtering was investigated.The chemical states and bonding characteristics of
《会饮》是柏拉图对话之一，虽然篇幅不长，但历来被作为柏拉图中后期思想的代表作受到重视。再加上《会饮》所涉及的“爱”的主题的独特性，使得研讨《会饮》的文章可谓汗牛充栋，《
对于现代的读者来说,翻译那些有着超过两千年的历史的文本中,无论是由思路难以费解人们所书写的,改写的或者是编辑的文本,总会遇到很多的麻烦。在这个过程中,关于文本真实性
十月革命作为“政治宇宙的北斗星”(霍布斯鲍姆语),标的新的政治历史版图的生成,但随着苏联社会主义大厦的瓦解,资本主义发展到后工业社会,产业结构、社会生活、传播方式、艺
采用高能球磨结合等离子放电烧结技术制备了超细晶不锈钢/TiC复合材料,通过腐蚀电化学动电位扫描技术研究了超细晶不锈钢/TiC复合材料的电化学腐蚀行为,SEM、EDS等微观分析手
复杂性科学作为“21世纪的科学”，一直是现代科学的重要组成部分，其理论的研究范围已远远超出了本身，并广泛深入的应用于各个学科领域，成为一种跨学科的方法论。因此，复杂性科学从