【摘 要】
：
A new ultrasonic three-point bending fatigue test device was introduced to investigate fatigue life ranging up to 1010 cycles and associated fracture behavior o
【机 构】
：
School of Electromechanics,Department of Mechanical Engineering
论文部分内容阅读
A new ultrasonic three-point bending fatigue test device was introduced to investigate fatigue life ranging up to 1010 cycles and associated fracture behavior of Ti-Al alloy. Tests were performed at a frequency of 20kHz with stress ratio R=0.5 and R=0.7 at ambient temperature in air. Three groups of specimens with different surface roughness were applied to investigate the effect of surface roughness on fatigue life. Furthermore, optical microscopy (OM) and scanning electron microscopy (SEM) were used for microstructure characteristic and fracture surface analysis. The S-N curves obtained show that fatigue failure occurs in the range of 105-1010 cycles, and the asymptote of S-N curve inclines slightly in very high cycle regime, but is not horizontal for R=0.5. Fatigue limit appears after 108 cycles for R=0.7. Surface roughness (the maximum roughness is no more than 3μm) has no influence on the fatigue properties in the high cycle regime. A detailed investigation on fatigue fracture surface shows that the Ti-Al alloy studied here is a binary alloy in the microstructure composed of α2-Ti3Al and γ-Ti-Al with fully lamellar microstructure. Fractography shows that fatigue failures are mostly initiated on the surface of specimens, also, in very high cycle regime, subsurface fatigue crack initiation can be found. Interlamellar fatigue crack initiation is predominant in the Ti-Al alloy with fully lamellar structure. Fatigue crack growth is mainly in transgranular mode.
其他文献
The Gd2O2CO3:Eu3+ with type-II structure phosphor was successfully synthesized via flux method at 400℃ and their photoluminescence properties in vacuum ultravi
Microstructure strongly influences the mechanical properties of cast iron. By inoculating the melt with proper inoculants, foreign substrates are brought into t
Based on the experimental data of apparent viscosity about semi-solid A356 aluminum alloy,the apparent viscosity model was developed and inserted into a commerc
The phase selection of ternary intermetallic compound τ phase (Mg32 (Al,Zn)49) and φ phase (A12Mg5Zn2) in high zinc magnesium alloys was studied by using scan
The formation mechanism of chunky graphite has been reviewed and studied. The study consisted of a unidirectional solidification method, a small droplet method
Skutterudite CoAs3 is a potentially important thermoelectric material. Morse potential is employed here to carry out molecular dynamics simulations of nanobulk
The effect of Sn addition on the microstructures and mechanical properties of Mg-5Al-2Si alloys was investi- gated with variations of Sn contents (3 and 6 wt pc
Chemical vapor deposition growth of one-dimensional nanomaterials usually demands substrates that have been coated with a layer of catalyst film. In this study,
Construction of integrated database including casting shapes with their casting design,technical knowledge, and thermophysical properties of the casting alloys
The microstructures of Ti6A14V alloy after hydrogenation were investigated by optical microscopy (OM), X-ray diffraction (XRD) and transmission electron microsc