本文分析了连铸过程中钢水增碳的原因,富碳层是钢水增碳的主要原因。论述了保护渣的溶化机理,并研究了保护渣富碳层的形成机理。
In this paper, the reasons for the increase of carbon in molten steel during continuous casting are analyzed, and the carbon-rich layer is the main reason for adding carbon by molten steel. The melting mechanism of mold flux was discussed, and the formation mechanism of flux-rich carbon layer was also studied.