【摘 要】
：
在ＺｒＯ２与４０Ｃｒ钢之间分别加入缓冲层Ｎｉ、４Ｊ３３、Ｔｉ和Ｃｕ进行钎焊连接。结果发现：缓冲层４Ｊ３３和纯Ｎｉ的化学元素会破坏钎料对陶瓷的浸润性，从而影响了钎料与ＺｒＯ２的界面反应，导致ＺｒＯ２／４０Ｃｒ钢连接失败。而缓冲层Ｃｕ和Ｔｉ不会影响钎料
论文部分内容阅读
在ＺｒＯ２与４０Ｃｒ钢之间分别加入缓冲层Ｎｉ、４Ｊ３３、Ｔｉ和Ｃｕ进行钎焊连接。结果发现：缓冲层４Ｊ３３和纯Ｎｉ的化学元素会破坏钎料对陶瓷的浸润性，从而影响了钎料与ＺｒＯ２的界面反应，导致ＺｒＯ２／４０Ｃｒ钢连接失败。而缓冲层Ｃｕ和Ｔｉ不会影响钎料对陶瓷的浸润性，又能释放接头的残余应力，可提高ＺｒＯ２／４０Ｃｒ钢接头强度。
Niobium, 4J33, Ti and Cu were brazed respectively between ZrO2 and 40Cr steel. The results show that the chemical elements of buffer layer 4J33 and pure Ni destroy the wettability of the brazing filler metal to the ceramic, which affects the interfacial reaction between the brazing filler metal and ZrO2, resulting in the failure of ZrO2 / 40Cr steel connection. The buffer layer of Cu and Ti will not affect the brazing filler metal on the ceramic, but also release the residual stress joints can improve the ZrO2 / 40Cr steel joint strength.
其他文献
介绍了生产过程中圆盘剪溜槽工作原理、卡钢原因分析、改进方法及改进后效果。
The working principle of the disc cutter chute in the production process, the reason a
广大农村实行家庭联产承包责任制以后,农村经济充满生机和活力,家庭经营已显示出它强盛的生命力。值得指出的是,作为农村合作经济双层经营的另一个层次,即村级经济的实力仍
抗日战争胜利后，中国司法界活跃着一位年轻的审判长。他英姿勃勃，穿梭于沪宁司法界，主审了为虎作伥的四大汉奸缨斌、陈公博、陈璧君、褚民谊；主审并使罪大恶极的日本战犯酒井隆、
本刊讯日前，中共中央政治局常委、国务院总理、国家信息化领导小组组长朱?基主持召开了国家信息化领导小组第一次会议。他指出，要高度重视，加强统筹协调，坚持面向市场，防止重复建
本文首次报道用安培电化学检测器探讨毛细管电泳分离的场放大进样效应，分析了系统峰的形成以及场放大进样对电泳分离检测的影响。采用25μm内径毛细管电泳分离，对去甲肾上腺素（N
走近作者孙慧玲,香港大学荣誉文学学士及教育硕士,著名儿童文学作家,报刊专栏作家,担任多项海内外写作比赛评判员,擅长儿童、少年励志故事及成长小说的创作,出版作品四十多种
糖皮质激素(简称激素)在结核性脑膜炎(简称结脑)中的治疗作用已被公认,尤其是对急性期结脑,激素已被广泛地应用于临床。但是,对激素剂量的选择,应用的时间等问题看法不一。
应用余氏理论计算了不同温度下有序与无序TiAl化合物的价电子结构，分析了温度升高引起的晶格膨胀、长程有序度P和短程有序度r下降对TiAl强度的影响。结果表明，TiAl化合物的R现
患者女,21d,以颜面进行性苍白10d于1987年2月20日入院。患儿系1胎1产,分娩史无异常,牛奶喂养。于10d前患儿面色即显苍白且进行性加重,因不烧、不咳、吃奶好未予注意,后因面
性早熟是一种性发育异常,我院1987年以来遇到35例,报导并讨论如下。 临床资料 一、真性性早熟11例,占本组31.42％,女孩
Precocious puberty is a sexual dysplasia, our hosp