【摘 要】
：
焊接高强度钢坯在粗轧时开裂,采用金相显微镜和扫描电镜对开裂钢坯进行了观察和分析。结果表明,同批次的钢坯存在中间裂纹和中心等轴晶区的偏移,开裂钢坯的表面和截面均观察
论文部分内容阅读
焊接高强度钢坯在粗轧时开裂,采用金相显微镜和扫描电镜对开裂钢坯进行了观察和分析。结果表明,同批次的钢坯存在中间裂纹和中心等轴晶区的偏移,开裂钢坯的表面和截面均观察到砷富集的现象;分析认为钢坯上下板面冷却速度的不同导致钢坯内部存在较大的内应力,在拉坯时树枝晶间产生中间裂纹,并在粗轧时导致钢坯开裂,而砷富集则导致网状热裂纹的形成。
High-strength welded billet cracking during rough rolling, the use of metallographic microscope and scanning electron microscope cracking billet was observed and analyzed. The results show that the same batch of billets exist intermediate cracks and center equiaxed zone offset, the surface and cross section of the cracked billet were observed arsenic enrichment phenomenon; Analysis of the billet cooling rate on the upper and lower plates lead to the internal billet The larger internal stress produces intermediate cracks between the dendrite during casting and leads to cracking of the billet during rough rolling, while the arsenic enrichment leads to the formation of reticular hot cracks.
其他文献
除了聚乳酸系生物降解塑料工业化生产规模最大的美国卡吉尔一道公司外,Fhahshell公司以淀粉、再生纤维素、生物降解聚合物等原料,生产复合涂层体系的生物降解塑料,其所属的M
摘 要：农产品是农业经济的重要组成部分，也是人们日常生活的必需品，但是现在的农产品质量安全问题已经严重威胁到了人们的生命安全，引起人们的高度关注，因此，农产品质量安全监管工作势在必行。本文重点分析了在新形势下农产品质量安全监管工作中遇到的难点，提出几点合理化建议，旨在改进农产品质量安全监管工作。 关键词：新形势；农产品；质量安全；监管难点；合理化建议 近年来，农产品和食品安全问题事件频频发生，
利用聚合硫酸铁(PFS)和壳聚糖(CTS)复合絮凝剂絮凝处理焦化二沉池废水,通过控制复合絮凝剂组成、投加量、pH值及搅拌速度等因素,对废水絮凝效果进行了分析.实验结果表明,在最
澳洲某矿焦煤具有较高的粘结性和丰富的胶质体,国内大多焦化企业将其作为优质焦煤配用.经煤质分析发现,该矿点焦煤流动度低,仅256 ddpm,膨胀度高,坩埚自由膨胀序数(CSN)达9,
Mister Important Design是一家专业从事酒店、餐厅、酒吧等空间设计的公司,由设计总监Charles Doell成立于2005年,他们致力于为业主创造出充满活力与热情的空间,通过独特的
针对武汉平煤武钢联合焦化有限责任公司的4套配煤系统的配煤细度(80％～82％)过高,无法满足焦炉生产需求的问题,通过实行选择性粉碎生产方式,将1号和3号配煤系统配合煤细度降低到68
鄂钢焦化公司在6 m焦炉上进行了用贫瘦煤替代瘦煤的炼焦试生产,考察了贫瘦煤配入量对焦炭质量及配煤成本的影响.试验表明:用贫瘦煤替代瘦煤炼焦,有利于吨焦配煤成本的下降,在
通过粘结指数试验以及配煤炼焦试验分析,探讨了不粘煤参与配煤炼焦的合适粒度范围,同时提出不粘煤参与配煤炼焦需要胶质体含量较高,必须对常规配煤结构进行调整.
武钢8号高炉投产4年多来一直保持良好操作炉型,对8号高炉的维护经验进行总结,认为合理的高炉炉型设计及生产维护是保证良好操作炉型的关键,介绍了武钢8号高炉维持良好操作炉
研究了焦粉与无烟煤作为烧结生产燃料时对烧结生产过程、烧结矿产量和质量产生的影响。结果表明:使用焦粉作固体燃料比使用无烟煤作固体燃料,适宜的固体燃料配比高0.3%,混合