【摘 要】
：
Laser powder bed fusion (L-PBF) was utilized to produce specimens in Ti-6Al-4V,which were subjected to a bi-lamellar heat treatment,which produces microstructur
【机 构】
：
Department of Mechanical Engineering,Technical University of Denmark,Produktionstorvet,Building 425,
论文部分内容阅读
Laser powder bed fusion (L-PBF) was utilized to produce specimens in Ti-6Al-4V,which were subjected to a bi-lamellar heat treatment,which produces microstructures consisting of primary α-lamellae and a fine secondary α-phase inside the inter-lamellar β-regions.The bi-lamellar microstructure was obtained as (i)a direct bi-lamellar heat treatment from the asbuilt condition or (ii) a bi-lamellar heat treatment preceded by a β-homogenization.For the bi-lamellar treatment with β-homogenization,cooling rates in the range 1-500 K/min were applied after homogenization in β-region followed by inter-critical annealing in the α + β region at various temperatures in the range 850-950 ℃.The microstructures were characterized using various microscopical techniques.Mechanical testing with Vickers hardness indentation and tensile testing was performed.The bi-lamellar microstructure was harder when compared to a soft fully lamellar microstructure,because of the presence of fine α-platelets inside the β-lamellae.Final low temperature ageing provided an additional hardness increase by precipitation hardening of the primary α-regions.The age hardened bi-lamellar microstructure shows a similar hardness as the very fine,as-built martensitic microstructure.The bi-lamellar microstructure has more favorable mechanical properties than the as-built condition,which has high strength,but poor ductility.After the bi-lamellar heat treatment,the elongation was improved by more than 250 ％.Due to the very high strength of the as-built condition,loss of tensile strength is unavoidable,resulting in a reduction of tensile strength of～18 ％.
其他文献
港口位于海运生态系统的核心层,对港口竞争力进行评价有助于掌握港口竞争优势及短板,从而提升港口竞争力,提升海运生态系统竞争力。港口竞争力评价是一项复杂的多属性评价问题,在深入分析港口竞争力影响因素的基础上,设计了考虑港城共荣的港口竞争力评价指标体系。采用标准离差率确定指标的权重,并通过证据推理法进行评价信息的融合,实现对港口竞争力的评价。以大连港和上海港为例,通过编程计算得到了两港口竞争力的评价结果,并进一步探索影响大连港、上海港港口竞争力水平增长驱动力的原因,为补齐竞争力发展短板提供相应建议。
Owing to its favorable thermodynamics and high density,NaAlH4 has been widely regarded as a potential hydrogen storage material,but its practical application is
The discovery of new materials is one of the driving forces to promote the development of modern society and technology innovation,the traditional materials res
The phase equilibria and thermodynamic properties of the U-Nb system were investigated through experiments and thermodynamic modeling.In the experiments,a serie
Marine biofouling is a major issue deteriorating the service performance and lifespan of marine infrastruc-tures.The development of a durable,long-term,and envi
This work aims at understanding the features of the Sn grains from which whiskers preferentially grow.The growth behavior of Sn whiskers on a 50 μm thick hyper
In recent years,the Ti2AlNb-based alloys are selected as potential alloys for elevated temperature appli-cations to replace conventional Ni-based superalloys ow
Public safety incidents caused by bacterial infections have attracted widespread attention towards antibacterial textiles (fibers,fabrics,etc.).Nevertheless,it
So far,only two orientation relationships(OR)between hexagonal close-packed(HCP)(αphase)and facecentered cubic(FCC)structures in zirconium and titanium alloys have been reported.Here a new type FCC phase(named γ phase)with OR:<11■0>α‖<
本文针对2×660 MW机组锅炉送风机在正常运行过程中出现由叶片断裂造成的设备运行参数异常,进行原因分析,并结合断裂原因总结本次送风机叶片断裂事故的教训,从而为后续或同类型风机设备的检修提供参考依据。