The dispersing process of polyacenic semiconductor(PAS) in polyethylene(PE) was simulated by using molecular dynamics(MD) methods. The results show that this process can be divided into three stages. In the first stage, PAS particles in the crystal region of PE are expelled to the amorphous region; in the second stage, PAS particles aggregate due to small surface areas and PE chains are adjusted continuously, which makes the crystal region complete; PAS particles are separated from each other and the total energy increases in the third stage. During the whole dispersing process, PAS particles are more stable in the amorphous region than in the crystal region. All the simulation results are in good agreement with the experimental results.
The dispersing process of polyacenic semiconductor (PAS) in polyethylene (PE) was simulated by using molecular dynamics (MD) methods. The results show that this process can be divided into three stages. In the first stage, PAS particles in the crystal region of PE is expelled to the amorphous region; in the second stage, PAS particles aggregate due to small surface areas and PE chains are adjusted continuously, which makes the crystal region complete; PAS particles are separated from each other and the total energy increases in the third During the whole dispersing process, PAS particles are more stable in the amorphous region than in the crystal region. All the simulation results are in good agreement with the experimental results.